Determination of α lamellae orientation in a β-Ti alloy using electron backscatter diffraction
© Petr Harcuba et al. 2024.
| Veröffentlicht in: | Journal of applied crystallography. - 1998. - 57(2024), Pt 4 vom: 01. Aug., Seite 1001-1010 |
|---|---|
| 1. Verfasser: | |
| Weitere Verfasser: | , , , |
| Format: | Online-Aufsatz |
| Sprache: | English |
| Veröffentlicht: |
2024
|
| Zugriff auf das übergeordnete Werk: | Journal of applied crystallography |
| Schlagworte: | Journal Article habit planes metastable titanium alloys orientation relationships α phase |
| Zusammenfassung: | © Petr Harcuba et al. 2024. The spatial orientation of α lamellae in a metastable β-Ti matrix of Timetal LCB (Ti-6.8 Mo-4.5 Fe-1.5 Al in wt%) was examined and the orientation of the hexagonal close-packed α lattice in the α lamella was determined. For this purpose, a combination of methods of small-angle X-ray scattering, scanning electron microscopy and electron backscatter diffraction was used. The habit planes of α laths are close to {111}β, which corresponds to (1320)α in the hexagonal coordinate system of the α phase. The longest α lamella direction lies approximately along one of the 〈110〉β directions which are parallel to the specific habit plane. Taking into account the average lattice parameters of the β and α phases in aged conditions in Timetal LCB, it was possible to index all main axes and faces of an α lath not only in the cubic coordinate system of the parent β phase but also in the hexagonal system of the α phase |
|---|---|
| Beschreibung: | Date Revised 08.08.2024 published: Electronic-eCollection Citation Status PubMed-not-MEDLINE |
| ISSN: | 0021-8898 |
| DOI: | 10.1107/S160057672400400X |