Atmospheric Pressure Plasma Deposition of Hydrophilic/Phobic Patterns and Thin Film Laminates on Any Surface
Patterned and layered hydrophilic/phobic coatings were deposited on multiple surfaces using nonfluorinated precursors (AA, acrylic acid; PMA, propargyl methacrylate) with an atmospheric pressure dielectric barrier discharge operating in open air. Water contact angles of the resulting films could be...
| Veröffentlicht in: | Langmuir : the ACS journal of surfaces and colloids. - 1992. - 35(2019), 30 vom: 30. Juli, Seite 9677-9683 |
|---|---|
| 1. Verfasser: | |
| Weitere Verfasser: | , , , , , , |
| Format: | Online-Aufsatz |
| Sprache: | English |
| Veröffentlicht: |
2019
|
| Zugriff auf das übergeordnete Werk: | Langmuir : the ACS journal of surfaces and colloids |
| Schlagworte: | Journal Article |
| Zusammenfassung: | Patterned and layered hydrophilic/phobic coatings were deposited on multiple surfaces using nonfluorinated precursors (AA, acrylic acid; PMA, propargyl methacrylate) with an atmospheric pressure dielectric barrier discharge operating in open air. Water contact angles of the resulting films could be tuned from <5° (superhydrophilic) to >135° (very hydrophobic) by adjusting the AA/PMA feed ratio and/or via postdeposition exposure of films to an Ar/O2 plasma treatment. Coatings could be applied to any surface and were seen to be water stable, due in large part to cross-linking induced from the reactivity of the PMA pendant groups. Hybrid hydrophilic/phobic patterns at submillimeter length scales, and philic/phobic/philic laminates were produced using a shadow mask and sequential deposition, respectively. Chemical heterogeneity of films was assessed using XPS, SIMS, and micro-IR imaging and suggest that localization of COOH and OH groups are primarily responsible for hydrophilicity. Overall, this work demonstrates that atmospheric pressure plasma polymerization is a simple and scalable method for robust and tunable control of wettability of surfaces of all kinds |
|---|---|
| Beschreibung: | Date Revised 23.09.2019 published: Print-Electronic Citation Status PubMed-not-MEDLINE |
| ISSN: | 1520-5827 |
| DOI: | 10.1021/acs.langmuir.9b00493 |