Highly Oriented J-Aggregates of Nitroazo Dye and Its Surface-Induced Chromism
Highly oriented J-aggregates of a nitroazo dye were obtained in solid thin films on aligned poly(tetrafluoroethylene) surfaces. During film deposition on a friction-transferred poly(tetrafluoroethylene) layer, a sharp peak grew in the polarized absorption spectra around 613 nm, which was red-shifted...
| Veröffentlicht in: | Langmuir : the ACS journal of surfaces and colloids. - 1992. - 32(2016), 19 vom: 17. Mai, Seite 4710-8 |
|---|---|
| 1. Verfasser: | |
| Weitere Verfasser: | , , |
| Format: | Online-Aufsatz |
| Sprache: | English |
| Veröffentlicht: |
2016
|
| Zugriff auf das übergeordnete Werk: | Langmuir : the ACS journal of surfaces and colloids |
| Schlagworte: | Journal Article |
| Zusammenfassung: | Highly oriented J-aggregates of a nitroazo dye were obtained in solid thin films on aligned poly(tetrafluoroethylene) surfaces. During film deposition on a friction-transferred poly(tetrafluoroethylene) layer, a sharp peak grew in the polarized absorption spectra around 613 nm, which was red-shifted 117 nm from the peak in dilute dichloromethane solution. The peak showed remarkable optical anisotropy: dichroic ratios D of up to 22 were observed, and the intrinsic D value should substantially exceed this value. These results indicate that the peak is attributable to highly oriented J-aggregates. On glass, however, H-like aggregates grew, exhibiting an absorption peak at 410 nm. Hence, the substrate surface induced the remarkable chromism observed as a 203 nm red shift |
|---|---|
| Beschreibung: | Date Completed 18.05.2018 Date Revised 18.05.2018 published: Print-Electronic Citation Status PubMed-not-MEDLINE |
| ISSN: | 1520-5827 |
| DOI: | 10.1021/acs.langmuir.6b00289 |