New bactericidal surgical suture coating
This paper demonstrates the effectiveness of a new antimicrobial suture coating. An amphiphilic polymer, poly[(aminoethyl methacrylate)-co-(butyl methacrylate)] (PAMBM), inspired by antimicrobial peptides, was bactericidal against S. aureus in time-kill experiments. PAMBM was then evaluated in a v...
| Veröffentlicht in: | Langmuir : the ACS journal of surfaces and colloids. - 1992. - 28(2012), 33 vom: 21. Aug., Seite 12134-9 |
|---|---|
| 1. Verfasser: | |
| Weitere Verfasser: | , , , , , |
| Format: | Online-Aufsatz |
| Sprache: | English |
| Veröffentlicht: |
2012
|
| Zugriff auf das übergeordnete Werk: | Langmuir : the ACS journal of surfaces and colloids |
| Schlagworte: | Journal Article Research Support, Non-U.S. Gov't Research Support, U.S. Gov't, Non-P.H.S. Anti-Bacterial Agents Polymers Stearic Acids stearic acid 4ELV7Z65AP Triclosan 4NM5039Y5X |
| Zusammenfassung: | This paper demonstrates the effectiveness of a new antimicrobial suture coating. An amphiphilic polymer, poly[(aminoethyl methacrylate)-co-(butyl methacrylate)] (PAMBM), inspired by antimicrobial peptides, was bactericidal against S. aureus in time-kill experiments. PAMBM was then evaluated in a variety of polymer blends using the Japanese Industrial Standard (JIS) method and showed excellent antimicrobial activity at a low concentration (0.5 wt %). Using a similar antimicrobial coating formula to commercial Vicryl Plus sutures, disk samples of the coating material containing PAMBM effectively killed bacteria (98% reduction at 0.75 wt %). Triclosan, the active ingredient in Vicryl Plus coatings, did not kill the bacteria. Further Kirby-Bauer assays of these disk samples showed an increasing zone of inhibition with increasing concentration of PAMBM. Finally, the PAMBM-containing coating was applied to sutures, and the morphology of the coating surface was characterized by SEM, along with Vicryl and uncoated sutures. The PAMBM-containing sutures killed bacteria more effectively (3 log(10) reduction at 2.4 wt %) than Vicryl Plus sutures (0.5 log(10) reduction) |
|---|---|
| Beschreibung: | Date Completed 28.12.2012 Date Revised 28.09.2017 published: Print-Electronic Citation Status MEDLINE |
| ISSN: | 1520-5827 |
| DOI: | 10.1021/la302732w |