Fabrication of electrochemical transistor based on pi-conjugate polymer Langmuir-Blodgett film
We fabricated an efficient organic electrochemical transistor (OECT) composed of polymer Langmuir-Blodgett (LB) film. The pi-conjugated polymer LB film, which was constructed from a poly(N-dodecylacrylamide) (pDDA) and poly(3-hexylthiophene) (PHT) mixture, was used as a conduction channel layer to c...
| Veröffentlicht in: | Langmuir : the ACS journal of surfaces and colloids. - 1992. - 23(2007), 16 vom: 31. Juli, Seite 8602-6 |
|---|---|
| 1. Verfasser: | |
| Weitere Verfasser: | , , |
| Format: | Aufsatz |
| Sprache: | English |
| Veröffentlicht: |
2007
|
| Zugriff auf das übergeordnete Werk: | Langmuir : the ACS journal of surfaces and colloids |
| Schlagworte: | Journal Article Research Support, Non-U.S. Gov't Membranes, Artificial Polyethylenes Quaternary Ammonium Compounds poly-N,N-dimethyl-N,N-diallylammonium chloride 26062-79-3 |
| Zusammenfassung: | We fabricated an efficient organic electrochemical transistor (OECT) composed of polymer Langmuir-Blodgett (LB) film. The pi-conjugated polymer LB film, which was constructed from a poly(N-dodecylacrylamide) (pDDA) and poly(3-hexylthiophene) (PHT) mixture, was used as a conduction channel layer to connect source and drain electrodes. The mixed-polymer LB film was characterized using UV-vis spectroscopy, X-ray diffraction (XRD), atomic force microscopy (AFM), and cyclic voltammetry. Subsequent UV spectra measurements, XRD measurements, and AFM measurements show that PHT forms a crystalline lamellar domain in the layered structure of pDDA. The OECT included 10 layers of the mixed-polymer LB film as the conduction channel layer. The OECT showed an on/off ratio of 1.1x10(4) and mobility of 7.5x10(-2) cm2 V(-1) s(-1) at low gate (VG=-1.2 V) and source-drain voltages (VDS=-0.5 V). Moreover, the necessary charge to operate the OECT was 1.1x10(-9) mol of e(-1) cm(-2), which was 2 orders smaller than the value reported using a similar device structure. The relatively high on/off ratio and low charge consumption suggest that this OECT, which is fabricated from pi-conjugated polymer LB films, is applicable to macroelectronic devices |
|---|---|
| Beschreibung: | Date Completed 02.10.2007 Date Revised 19.11.2009 published: Print-Electronic Citation Status MEDLINE |
| ISSN: | 1520-5827 |