Thin films of bicontinuous cubic mesostructured silica templated by a nonionic surfactant
Thin films ofbicontinuous cubic mesostructured silica were formed using the nonionic poly(oxyethylene)-alkyl ether surfactant Brij-56 as a structure-directing agent. The synthesis conditions were chosen such that the estimated volume fraction of surfactant in the silica/surfactant films corresponded...
| Veröffentlicht in: | Langmuir : the ACS journal of surfaces and colloids. - 1992. - 20(2004), 14 vom: 06. Juli, Seite 5998-6004 |
|---|---|
| 1. Verfasser: | |
| Weitere Verfasser: | , , |
| Format: | Aufsatz |
| Sprache: | English |
| Veröffentlicht: |
2004
|
| Zugriff auf das übergeordnete Werk: | Langmuir : the ACS journal of surfaces and colloids |
| Schlagworte: | Journal Article |
| Zusammenfassung: | Thin films ofbicontinuous cubic mesostructured silica were formed using the nonionic poly(oxyethylene)-alkyl ether surfactant Brij-56 as a structure-directing agent. The synthesis conditions were chosen such that the estimated volume fraction of surfactant in the silica/surfactant films corresponded approximately to the composition at which the bicontinuous cubic phase occurs in the water/surfactant phase diagram. Small-angle X-ray scattering and transmission electron microscopy measurements reveal that the cubic phase corresponds to the Ia3(-)d double-gyroid structure, with some distortion due to anisotropic film shrinkage. The cubic structure grows as faceted domains that are well-oriented with respect to the substrate and often occur in coexistence with a lamellar phase. By adjusting the temperature at which the films are aged, it is possible to create films with 2D hexagonal, cubic, or lamellar structures at a single composition |
|---|---|
| Beschreibung: | Date Completed 20.03.2007 Date Revised 26.10.2019 published: Print Citation Status PubMed-not-MEDLINE |
| ISSN: | 1520-5827 |