Characteristics of bricks made from waste steel slag

The characteristics of bricks made from steel slag were investigated in this research. Slag addition was shown to reduce the required firing temperature. When the firing temperature was greater than 1050 degrees C and the slag addition less than 10%, the bricks met ROC national standard CNS 3319 thi...

Ausführliche Beschreibung

Bibliographische Detailangaben
Veröffentlicht in:	Waste management (New York, N.Y.). - 1999. - 24(2004), 10 vom: 29., Seite 1043-7
1. Verfasser:	Shih, Pai-Haung (VerfasserIn)
Weitere Verfasser:	Wu, Zong-Zheng, Chiang, Hung-Lung
Format:	Aufsatz
Sprache:	English
Veröffentlicht:	2004
Zugriff auf das übergeordnete Werk:	Waste management (New York, N.Y.)
Schlagworte:	Journal Article Aluminum Silicates Industrial Waste Water 059QF0KO0R Steel 12597-69-2 Clay T1FAD4SS2M


LEADER	01000caa a22002652 4500
001	NLM152343687
003	DE-627
005	20250206013045.0
007	tu
008	231223s2004 xx \|\|\|\|\| 00\| \|\|eng c
028	5	2	\|a pubmed25n0508.xml
035			\|a (DE-627)NLM152343687
035			\|a (NLM)15567669
040			\|a DE-627 \|b ger \|c DE-627 \|e rakwb
041			\|a eng
100	1		\|a Shih, Pai-Haung \|e verfasserin \|4 aut
245	1	0	\|a Characteristics of bricks made from waste steel slag
264		1	\|c 2004
336			\|a Text \|b txt \|2 rdacontent
337			\|a ohne Hilfsmittel zu benutzen \|b n \|2 rdamedia
338			\|a Band \|b nc \|2 rdacarrier
500			\|a Date Completed 15.11.2005
500			\|a Date Revised 01.12.2018
500			\|a published: Print
500			\|a Citation Status MEDLINE
520			\|a The characteristics of bricks made from steel slag were investigated in this research. Slag addition was shown to reduce the required firing temperature. When the firing temperature was greater than 1050 degrees C and the slag addition less than 10%, the bricks met ROC national standard CNS 3319 third-class brick for builders. The percentage of slag increased as the quartz and kaolin decreased in the sintered samples while the magnesium aluminum silicate and calcium silicate increased. There were no new crystal phases observed in these samples
650		4	\|a Journal Article
650		7	\|a Aluminum Silicates \|2 NLM
650		7	\|a Industrial Waste \|2 NLM
650		7	\|a Water \|2 NLM
650		7	\|a 059QF0KO0R \|2 NLM
650		7	\|a Steel \|2 NLM
650		7	\|a 12597-69-2 \|2 NLM
650		7	\|a Clay \|2 NLM
650		7	\|a T1FAD4SS2M \|2 NLM
700	1		\|a Wu, Zong-Zheng \|e verfasserin \|4 aut
700	1		\|a Chiang, Hung-Lung \|e verfasserin \|4 aut
773	0	8	\|i Enthalten in \|t Waste management (New York, N.Y.) \|d 1999 \|g 24(2004), 10 vom: 29., Seite 1043-7 \|w (DE-627)NLM098197061 \|x 0956-053X \|7 nnns
773	1	8	\|g volume:24 \|g year:2004 \|g number:10 \|g day:29 \|g pages:1043-7
912			\|a GBV_USEFLAG_A
912			\|a SYSFLAG_A
912			\|a GBV_NLM
912			\|a GBV_ILN_350
951			\|a AR
952			\|d 24 \|j 2004 \|e 10 \|b 29 \|h 1043-7