Characteristics of bricks made from waste steel slag
The characteristics of bricks made from steel slag were investigated in this research. Slag addition was shown to reduce the required firing temperature. When the firing temperature was greater than 1050 degrees C and the slag addition less than 10%, the bricks met ROC national standard CNS 3319 thi...
| Veröffentlicht in: | Waste management (New York, N.Y.). - 1999. - 24(2004), 10 vom: 29., Seite 1043-7 |
|---|---|
| 1. Verfasser: | |
| Weitere Verfasser: | , |
| Format: | Aufsatz |
| Sprache: | English |
| Veröffentlicht: |
2004
|
| Zugriff auf das übergeordnete Werk: | Waste management (New York, N.Y.) |
| Schlagworte: | Journal Article Aluminum Silicates Industrial Waste Water 059QF0KO0R Steel 12597-69-2 Clay T1FAD4SS2M |
| Zusammenfassung: | The characteristics of bricks made from steel slag were investigated in this research. Slag addition was shown to reduce the required firing temperature. When the firing temperature was greater than 1050 degrees C and the slag addition less than 10%, the bricks met ROC national standard CNS 3319 third-class brick for builders. The percentage of slag increased as the quartz and kaolin decreased in the sintered samples while the magnesium aluminum silicate and calcium silicate increased. There were no new crystal phases observed in these samples |
|---|---|
| Beschreibung: | Date Completed 15.11.2005 Date Revised 01.12.2018 published: Print Citation Status MEDLINE |
| ISSN: | 0956-053X |