Decoupling the Effects of Interface Chemical Degradation and Mechanical Cracking in Solid-State Batteries with Silicon Electrode

Decoupling the Effects of Interface Chemical Degradation and Mechanical Cracking in Solid-State Batteries with Silicon Electrode

© 2024 The Author(s). Advanced Materials published by Wiley‐VCH GmbH.

Bibliographische Detailangaben
Veröffentlicht in:Advanced materials (Deerfield Beach, Fla.). - 1998. - (2024) vom: 20. Dez., Seite e2415006
1. Verfasser: Huo, Hanyu (VerfasserIn)
Weitere Verfasser: Bai, Yang, Benz, Sebastian Leonard, Weintraut, Timo, Wang, Shuo, Henss, Anja, Raabe, Dierk, Janek, Jürgen
Format: Online-Aufsatz
Sprache:English
Veröffentlicht: 2024
Zugriff auf das übergeordnete Werk:Advanced materials (Deerfield Beach, Fla.)
Schlagworte:Journal Article chemo‐mechanics silicon anodes solid electrolytes solid‐state batteries
Beschreibung
Zusammenfassung:© 2024 The Author(s). Advanced Materials published by Wiley‐VCH GmbH.
Silicon is a promising negative electrode material for solid-state batteries (SSBs) due to its high specific capacity and ability to prevent lithium dendrite formation. However, SSBs with silicon electrodes currently suffer from poor cycling stability, despite chemical engineering efforts. This study investigates the cycling failure mechanism of composite Si/Li6PS5Cl electrodes by decoupling the effects of interface chemical degradation and mechanical cracking. Chlorine-rich Li5.5PS4.5Cl1.5 suppresses interface chemical degradation when paired with silicon, while small-grained Li6PS5Cl shows 4.3-fold increase of interface resistance due to large Si/Li6PS5Cl contact area for interface degradation. Despite this, small-grained Li6PS5Cl improves the microstructure homogeneity of the electrode composites, effectively alleviating the stress accumulation caused by the expansion/shrinkage of silicon particles. This minimizes bulk cracks in Li6PS5Cl during the lithiation processes and interface delamination during the delithiation processes. Mechanical cracking shows a dominant role in increasing interface resistance than interface chemical degradation. Therefore, electrodes with small-grained Li6PS5Cl show better cycling stability than those with Li5.5PS4.5Cl1.5. This work not only provides an approach to decouple the complex effects for cycling failure analysis but also provides a guideline for better use of silicon in negative electrodes of SSBs
Beschreibung:Date Revised 20.12.2024
published: Print-Electronic
Citation Status Publisher
ISSN:1521-4095
DOI:10.1002/adma.202415006