Intercalation Behavior of a Spiro-bipyrrolidinium Cation into a Graphite Electrode from Dimethyl/Propylene Carbonates
Quaternary ammonium-graphite intercalation compounds (QA+-GICs) are promising negative electrode materials in dual-carbon batteries by virtue of safety, low cost, and environmental friendliness. However, the intercalation behavior of QA+ into graphite electrodes in mixed solvents has never been repo...
| Veröffentlicht in: | Langmuir : the ACS journal of surfaces and colloids. - 1999. - 40(2024), 46 vom: 19. Nov., Seite 24585-24591 |
|---|---|
| 1. Verfasser: | |
| Weitere Verfasser: | , |
| Format: | Online-Aufsatz |
| Sprache: | English |
| Veröffentlicht: |
2024
|
| Zugriff auf das übergeordnete Werk: | Langmuir : the ACS journal of surfaces and colloids |
| Schlagworte: | Journal Article |
| Zusammenfassung: | Quaternary ammonium-graphite intercalation compounds (QA+-GICs) are promising negative electrode materials in dual-carbon batteries by virtue of safety, low cost, and environmental friendliness. However, the intercalation behavior of QA+ into graphite electrodes in mixed solvents has never been reported. Herein, spiro-(1,1')-bipyrrolidinium tetrafluoroborate dissolved in a dimethyl/propylene carbonate (DMC/PC) binary solvent system was employed in graphite/activated carbon (AC) capacitors. The storage behavior of the spiro-(1,1')-bipyrrolidinium cation into graphite is very related to the solvent composition of the electrolyte solutions. In situ X-ray diffraction tests revealed that the graphite electrodes can form different QA+-GICs during cycling, which is a key factor influencing the electrochemical performance of graphite/AC capacitors. Besides, the reversible thickness change of graphite in graphite/AC capacitors with different electrolytes during the charge-discharge process was also addressed. These findings provide sound evidence for the co-intercalation of the solvent with the cation |
|---|---|
| Beschreibung: | Date Revised 19.11.2024 published: Print-Electronic Citation Status PubMed-not-MEDLINE |
| ISSN: | 1520-5827 |
| DOI: | 10.1021/acs.langmuir.4c03435 |