Ultrathin Ni-Fe MOF Nanosheets : Efficient and Durable Water Oxidation at High Current Densities
Efficient, durable, and economical electrocatalysts are crucial for advancing energy technology by facilitating the oxygen evolution reaction (OER). Here, ultrathin Ni-Fe metal-organic skeleton (MOF) nanosheets were created in situ on nickel foam (NiFe-UMNs/NF). The catalyst exhibited excellent OER...
| Veröffentlicht in: | Langmuir : the ACS journal of surfaces and colloids. - 1999. - 40(2024), 25 vom: 25. Juni, Seite 13122-13133 |
|---|---|
| 1. Verfasser: | |
| Weitere Verfasser: | , , , , , |
| Format: | Online-Aufsatz |
| Sprache: | English |
| Veröffentlicht: |
2024
|
| Zugriff auf das übergeordnete Werk: | Langmuir : the ACS journal of surfaces and colloids |
| Schlagworte: | Journal Article |
| Zusammenfassung: | Efficient, durable, and economical electrocatalysts are crucial for advancing energy technology by facilitating the oxygen evolution reaction (OER). Here, ultrathin Ni-Fe metal-organic skeleton (MOF) nanosheets were created in situ on nickel foam (NiFe-UMNs/NF). The catalyst exhibited excellent OER catalytical abilities, with only 269 mV overpotentials at 250 mA cm-2. Besides, when integrated with Pt/C/NF, NiFe-UMNs/NF held the potential for application in industrial alkaline water electrolysis with an initial voltage retention of approximately 86% following a continuous operation of 100 h at a current density of 250 mA cm-2. The super performance of the NiFe-UMNs/NF catalyst was attributed to ultrathin morphology, super hydrophilicity, and synergistic effects between Ni and Fe within the MOF. In situ Raman showed that NiFe-UMNs were converted to NiFeOOH as the active species in the OER process. Density functional theory revealed that iron doping accelerated the rate-determining step and reduced the OER reaction energy barrier. This work elucidated a promising electrocatalyst for OER and enriched the practical implementation of MOF materials |
|---|---|
| Beschreibung: | Date Revised 25.06.2024 published: Print-Electronic Citation Status PubMed-not-MEDLINE |
| ISSN: | 1520-5827 |
| DOI: | 10.1021/acs.langmuir.4c01065 |