Hyper-Cross-Linked Resin Modified by a Micropore Polymer for Gas Adsorption and Separation
Polymerization confined to the pore was first adapted for the nanoscale structure adjustment of adsorption resin. The self-cross-linked polymer (P-1) formed in the pore of hyper-cross-linked resin (HR) by the Friedel-Crafts reaction of p-dichloroxylene (p-DCX), occupying the macropore of the HR resi...
| Veröffentlicht in: | Langmuir : the ACS journal of surfaces and colloids. - 1992. - 40(2024), 24 vom: 18. Juni, Seite 12465-12474 |
|---|---|
| 1. Verfasser: | |
| Weitere Verfasser: | , , , , , , |
| Format: | Online-Aufsatz |
| Sprache: | English |
| Veröffentlicht: |
2024
|
| Zugriff auf das übergeordnete Werk: | Langmuir : the ACS journal of surfaces and colloids |
| Schlagworte: | Journal Article |
| Zusammenfassung: | Polymerization confined to the pore was first adapted for the nanoscale structure adjustment of adsorption resin. The self-cross-linked polymer (P-1) formed in the pore of hyper-cross-linked resin (HR) by the Friedel-Crafts reaction of p-dichloroxylene (p-DCX), occupying the macropore of the HR resin and bringing about an external micropore. Compared with the raw HR resin, the volume of the micropore of HRP-1 in 0.4 < D < 1 nm increased but the volume of the macropore has obviously decreased. After the loading of P-1 in the nanopore of HR, HR@P-1 has better gas adsorption performance. At 298 and 100 KPa, the adsorption capacity of CO2 is almost 30% higher than that of HR, reaching 35.7 cm3/g, due to the increase in the smaller micropore volume. Moreover, HR@P-1 has also been found to be the first C2H6-selective adsorption resin. The uptake of C2H6 is up to 56 cm3/g, and the IAST selectivity of C2H6/CH4 reaches 15.3. HR@P-1 can also separate syngas efficiently at ambient temperature and be regenerated by simple vacuum operation |
|---|---|
| Beschreibung: | Date Revised 18.06.2024 published: Print-Electronic Citation Status PubMed-not-MEDLINE |
| ISSN: | 1520-5827 |
| DOI: | 10.1021/acs.langmuir.4c00863 |