Electrodeposited MoxSyOz/Ni Tribological Coatings
Deposition of molybdenum disulfide (MoS2) coatings using physical vapor deposition (PVD) and mechanical burnishing has been widely assessed for solid lubricants in space applications but still suffers from line-of-sight constraints on complex geometries. Here, we highlight one of the first demonstra...
| Veröffentlicht in: | Langmuir : the ACS journal of surfaces and colloids. - 1992. - 40(2024), 11 vom: 19. März, Seite 5776-5784 |
|---|---|
| 1. Verfasser: | |
| Weitere Verfasser: | , , , , , |
| Format: | Online-Aufsatz |
| Sprache: | English |
| Veröffentlicht: |
2024
|
| Zugriff auf das übergeordnete Werk: | Langmuir : the ACS journal of surfaces and colloids |
| Schlagworte: | Journal Article |
| Zusammenfassung: | Deposition of molybdenum disulfide (MoS2) coatings using physical vapor deposition (PVD) and mechanical burnishing has been widely assessed for solid lubricants in space applications but still suffers from line-of-sight constraints on complex geometries. Here, we highlight one of the first demonstrations of electrodeposited MoxSyOz and MoxSyOz/Ni thin-film coatings from aqueous solutions of ammonium tetrathiomolybdate for solid lubricant applications and their remarkable ability to provide low coefficients of friction and high wear resistance. Characterization of the coating morphology shows amorphous microstructures with a high oxygen content and cracking upon drying. Even so, electrodeposited MoxSyOz can achieve low steady-state coefficients of friction (μ ∼ 0.05-0.06) and wear rates (2.6 × 10-7 mm3/(N m)) approaching those of physical vapor deposited coatings (2.3 × 10-7 mm3/(N m)). Additionally, we show that adding dopants such as nickel increased the wear rate (7.5 × 10-7 mm3/(N m)) and initial coefficient of friction (μi = 0.23) due to compositional modifications such as dramatic sub-stoichiometry (S/Mo ∼ 1) and expression of a NiOx surface layer, although doping did reduce the degree of cracking upon drying |
|---|---|