A Heteroanionic Zinc Ion Conductor for Dendrite-Free Zn Metal Anodes
© 2023 Wiley-VCH GmbH.
| Publié dans: | Advanced materials (Deerfield Beach, Fla.). - 1998. - 35(2023), 18 vom: 22. Mai, Seite e2300195 |
|---|---|
| Auteur principal: | |
| Autres auteurs: | , , , , , , |
| Format: | Article en ligne |
| Langue: | English |
| Publié: |
2023
|
| Accès à la collection: | Advanced materials (Deerfield Beach, Fla.) |
| Sujets: | Journal Article anodization mixed anion compounds zinc anode protection zinc ion conductors |
| Résumé: | © 2023 Wiley-VCH GmbH. Although zinc-based batteries are promising candidates for eco-friendly and cost-effective energy storage devices, their performance is severely retarded by dendrite formation. As the simplest zinc compounds, zinc chalcogenides, and halides are individually applied as a Zn protection layer due to high zinc ion conductivity. However, the mixed-anion compounds are not studied, which constrains the Zn2+ diffusion in single-anion lattices to their own limits. A heteroanionic zinc ion conductor (Zny O1- x Fx ) coating layer is designed by in situ growth method with tunable F content and thickness. Strengthened by F aliovalent doping, the Zn2+ conductivity is enhanced within the wurtzite motif for rapid lattice Zn migration. Zny O1- x Fx also affords zincophilic sites for oriented superficial Zn plating to suppress dendrite growth. Therefore, Zny O1- x Fx -coated anode exhibits a low overpotential of 20.4 mV for 1000 h cycle life at a plating capacity of 1.0 mA h cm-2 during symmetrical cell test. The MnO2 //Zn full battery further proves high stability of 169.7 mA h g-1 for 1000 cycles. This work may enlighten the mixed-anion tuning for high-performance Zn-based energy storage devices |
|---|---|
| Description: | Date Completed 07.05.2023 Date Revised 07.05.2023 published: Print-Electronic Citation Status PubMed-not-MEDLINE |
| ISSN: | 1521-4095 |
| DOI: | 10.1002/adma.202300195 |