Multifunctionalized Cellulose Nanofiber for Water-Repellent and Wash-Sustainable Coatings on Fabrics
A new synthetic route was developed to modify cellulose nanofiber for water-repellent coatings with great sustainability after multiple washing cycles. Multiple functional groups were grafted on 2,2,6,6-tetramethylpiperidine 1-oxyl radical (TEMPO)-oxidized cellulose nanofibers (TOCN) to achieve supe...
| Veröffentlicht in: | Langmuir : the ACS journal of surfaces and colloids. - 1992. - 36(2020), 28 vom: 21. Juli, Seite 8144-8151 |
|---|---|
| 1. Verfasser: | |
| Weitere Verfasser: | , |
| Format: | Online-Aufsatz |
| Sprache: | English |
| Veröffentlicht: |
2020
|
| Zugriff auf das übergeordnete Werk: | Langmuir : the ACS journal of surfaces and colloids |
| Schlagworte: | Journal Article |
| Zusammenfassung: | A new synthetic route was developed to modify cellulose nanofiber for water-repellent coatings with great sustainability after multiple washing cycles. Multiple functional groups were grafted on 2,2,6,6-tetramethylpiperidine 1-oxyl radical (TEMPO)-oxidized cellulose nanofibers (TOCN) to achieve superhydrophobic performance and strong adhesion on cotton cloth. First, hexadecylamine (HDA) was used to modify TOCN surface into hydrophobic derivatives via amidation. The amidation-modified TOCN (AMT) were then grafted with a polyisocyanate cross-linking agent (PCA). The final multimodified TOCN (MMT) had hydrophobic alkyls and isocyanate groups on the surface. These surface functional groups were confirmed by Fourier transform infrared spectroscopy (FTIR) and X-ray photoelectron spectroscopy (XPS). After spraying the MMT suspension on cotton fabrics, the isocyanate groups would react with hydroxyl groups on cotton fibers, leading to a uniform conformal layer of MMT on fabric surfaces. The MMT coating showed great water repellence and washing sustainability. A large contact angle of 150° and a small sliding angle of ∼10° were observed. The superhydrophobic performance retained even after 10 laundry washing cycles. Several examples were also demonstrated to show the capability and the possibility of applying this coating material for water-repellent applications |
|---|---|
| Beschreibung: | Date Revised 21.07.2020 published: Print-Electronic Citation Status PubMed-not-MEDLINE |
| ISSN: | 1520-5827 |
| DOI: | 10.1021/acs.langmuir.0c01145 |