Improvement of Low-Temperature zT in a Mg3 Sb2 -Mg3 Bi2 Solid Solution via Mg-Vapor Annealing
© 2019 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.
| Publié dans: | Advanced materials (Deerfield Beach, Fla.). - 1998. - 31(2019), 35 vom: 25. Aug., Seite e1902337 |
|---|---|
| Auteur principal: | |
| Autres auteurs: | , , |
| Format: | Article en ligne |
| Langue: | English |
| Publié: |
2019
|
| Accès à la collection: | Advanced materials (Deerfield Beach, Fla.) |
| Sujets: | Journal Article Mg3Sb2 grain boundaries ionized impurities thermoelectrics vapor annealing |
| Résumé: | © 2019 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim. Materials with high zT over a wide temperature range are essential for thermoelectric applications. n-Type Mg3 Sb2 -based compounds have been shown to achieve high zT at 700 K, but their performance at low temperatures (<500 K) is compromised due to their highly resistive grain boundaries. Syntheses and optimization processes to mitigate this grain-boundary effect has been limited due to loss of Mg, which hinders a sample's n-type dopability. A Mg-vapor anneal processing step that grows a sample's grain size and preserves its n-type carrier concentration during annealing is demonstrated. The electrical conductivity and mobility of the samples with large grain size follows a phonon-scattering-dominated T-3/2 trend over a large temperature range, further supporting the conclusion that the temperature-activated mobility in Mg3 Sb2 -based materials is caused by resistive grain boundaries. The measured Hall mobility of electrons reaches 170 cm2 V-1 s-1 in annealed 800 °C sintered Mg3 + δ Sb1.49 Bi0.5 Te0.01 , the highest ever reported for Mg3 Sb2 -based thermoelectric materials. In particular, a sample with grain size >30 mm has a zT 0.8 at 300 K, which is comparable to commercial thermoelectric materials used at room temperature (n-type Bi2 Te3 ) while reaching zT 1.4 at 700 K, allowing applications over a wider temperature scale |
|---|---|