Debye-Waller coefficient of heavily deformed nanocrystalline iron
Synchrotron radiation X-ray diffraction (XRD) patterns from an extensively ball-milled iron alloy powder were collected at 100, 200 and 300 K. The results were analysed together with those using extended X-ray absorption fine structure, measured on the same sample at liquid nitrogen temperature (77 ...
Ausführliche Beschreibung
Bibliographische Detailangaben
| Veröffentlicht in: | Journal of applied crystallography. - 1998. - 50(2017), Pt 2 vom: 01. Apr., Seite 508-518
|
|---|
| 1. Verfasser: |
Scardi, P
(VerfasserIn) |
|---|
| Weitere Verfasser: |
Rebuffi, L,
Abdellatief, M,
Flor, A,
Leonardi, A |
|---|
| Format: | Online-Aufsatz
|
|---|
| Sprache: | English |
|---|
| Veröffentlicht: |
2017
|
|---|
| Zugriff auf das übergeordnete Werk: | Journal of applied crystallography
|
|---|
| Schlagworte: | Journal Article
Debye–Waller coefficient
EXAFS
molecular dynamics
nanocrystalline materials
plastically deformed materials
synchrotron radiation X-ray diffraction
temperature diffuse scattering |
|---|