One-Pot Synthesis of Fe(III)-Polydopamine Complex Nanospheres : Morphological Evolution, Mechanism, and Application of the Carbonized Hybrid Nanospheres in Catalysis and Zn-Air Battery
We report one-pot synthesis of Fe(III)-polydopamine (PDA) complex nanospheres, their structures, morphology evolution, and underlying mechanism. The complex nanospheres were synthesized by introducing ferric ions into the reaction mixture used for polymerization of dopamine. It is verified that both...
| Veröffentlicht in: | Langmuir : the ACS journal of surfaces and colloids. - 1992. - 32(2016), 36 vom: 13. Sept., Seite 9265-75 |
|---|---|
| 1. Verfasser: | |
| Weitere Verfasser: | , , , , , |
| Format: | Online-Aufsatz |
| Sprache: | English |
| Veröffentlicht: |
2016
|
| Zugriff auf das übergeordnete Werk: | Langmuir : the ACS journal of surfaces and colloids |
| Schlagworte: | Journal Article Research Support, Non-U.S. Gov't |
| Zusammenfassung: | We report one-pot synthesis of Fe(III)-polydopamine (PDA) complex nanospheres, their structures, morphology evolution, and underlying mechanism. The complex nanospheres were synthesized by introducing ferric ions into the reaction mixture used for polymerization of dopamine. It is verified that both the oxidative polymerization of dopamine and Fe(III)-PDA complexation contribute to the "polymerization" process, in which the ferric ions form coordination bonds with both oxygen and nitrogen, as indicated by X-ray absorption fine-structure spectroscopy. In the "polymerization" process, the morphology of the complex nanostructures is gradually transformed from sheetlike to spherical at the feed Fe(III)/dopamine molar ratio of 1/3. The final size of the complex spheres is much smaller than its neat PDA counterpart. At higher feed Fe(III)/dopamine molar ratios, the final morphology of the "polymerization" products is sheetlike. The results suggest that the formation of spherical morphology is likely to be driven by covalent polymerization-induced decrease of hydrophilic functional groups, which causes reself-assembly of the PDA oligomers to reduce surface area. We also demonstrate that this one-pot synthesis route for hybrid nanospheres enables the facile construction of carbonized PDA (C-PDA) nanospheres uniformly embedded with Fe3O4 nanoparticles of only 3-5 nm in size. The C-PDA/Fe3O4 nanospheres exhibit catalytic activity toward oxygen reduction reaction and deliver a stable discharge voltage for over 200 h when utilized as the cathode in a primary Zn-air battery and are also good recyclable catalyst supports |
|---|---|
| Beschreibung: | Date Completed 06.06.2018 Date Revised 06.06.2018 published: Print-Electronic Citation Status PubMed-not-MEDLINE |
| ISSN: | 1520-5827 |
| DOI: | 10.1021/acs.langmuir.6b02331 |