Gypsum blocks produced from TiO2 production by-products
Calcined titanium gypsum was investigated by the ways of XRD (powder X-ray diffraction), XRF (X-ray fluorescence) and TG-DTA (thermogravimetric-differential thermal analyses). It was employed as raw material for making lightweight materials. The influence of cement, amount of water/solid (W/S) ratio...
| Veröffentlicht in: | Environmental technology. - 1993. - 37(2016), 9 vom: 23., Seite 1094-100 |
|---|---|
| 1. Verfasser: | |
| Weitere Verfasser: | , , , , , |
| Format: | Online-Aufsatz |
| Sprache: | English |
| Veröffentlicht: |
2016
|
| Zugriff auf das übergeordnete Werk: | Environmental technology |
| Schlagworte: | Journal Article Research Support, Non-U.S. Gov't Titanium gypsum building materials gypsum blocks industrial wastes recycling Industrial Waste titanium dioxide 15FIX9V2JP mehr... |
| Zusammenfassung: | Calcined titanium gypsum was investigated by the ways of XRD (powder X-ray diffraction), XRF (X-ray fluorescence) and TG-DTA (thermogravimetric-differential thermal analyses). It was employed as raw material for making lightweight materials. The influence of cement, amount of water/solid (W/S) ratio, water-reducing agent, citric acid content and the hydration age on the gypsum blocks was investigated. The results showed that the optimum W/S ratio, cement content and water-reducing agent are 0.9, 10% and 2 wt% for the calcined gypsum from titanium gypsum, respectively. The 5.96 MPa was attained after 7 days of ageing. It was also found that the citric acid is inappropriate to be used in the production of gypsum blocks from TiO2 production by-products |
|---|---|
| Beschreibung: | Date Completed 13.12.2016 Date Revised 30.12.2016 published: Print-Electronic Citation Status MEDLINE |
| ISSN: | 1479-487X |
| DOI: | 10.1080/09593330.2015.1102329 |