Role of silicon nanowire diameter for alkyl (chain lengths C₁-C₁₈) passivation efficiency through Si-C bonds

The effect of silicon nanowire (Si NW) diameter on the functionalization efficiency as given by covalent Si-C bond formation is studied for two distinct examples of 25 ± 5 and 50 ± 5 nm diameters (Si NW25 and Si NW50, respectively). A two-step chlorination/alkylation process is used to connect alkyl...

Ausführliche Beschreibung

Bibliographische Detailangaben
Veröffentlicht in:Langmuir : the ACS journal of surfaces and colloids. - 1992. - 31(2015), 8 vom: 03. März, Seite 2430-7
1. Verfasser: Bashouti, Muhammad Y (VerfasserIn)
Weitere Verfasser: Garzuzi, Carmelina A, de la Mata, Maria, Arbiol, Jordi, Ristein, Jürgen, Haick, Hossam, Christiansen, Silke
Format: Online-Aufsatz
Sprache:English
Veröffentlicht: 2015
Zugriff auf das übergeordnete Werk:Langmuir : the ACS journal of surfaces and colloids
Schlagworte:Journal Article
Beschreibung
Zusammenfassung:The effect of silicon nanowire (Si NW) diameter on the functionalization efficiency as given by covalent Si-C bond formation is studied for two distinct examples of 25 ± 5 and 50 ± 5 nm diameters (Si NW25 and Si NW50, respectively). A two-step chlorination/alkylation process is used to connect alkyl chains of various lengths (C1-C18) to thinner and thicker Si NWs. The shorter the alkyl chain lengths, the larger the surface coverage of the two studied Si NWs. Increasing the alkyl chain length (C2-C9) changes the coverage on the NWs: while for Si NW25 90 ± 10% of all surface sites are covered with Si-C bonds, only 50 ± 10% of all surface sites are covered with Si-C bonds for the Si NW50 wires. Increasing the chain length further to C14-C18 decreases the alkyl coverage to 36 ± 6% in thin Si NW25 and to 20 ± 5% in thick Si NW50. These findings can be interpreted as being a result of increased steric hindrance of Si-C bond formation for longer chain lengths and higher surface energy for the thinner Si NWs. As a direct consequence of these findings, Si NW surfaces have different stabilities against oxidation: they are more stable at higher Si-C bond coverage, and the surface stability was found to be dependent on the Si-C binding energy itself. The Si-C binding energy differs according to (C1-9)-Si NW > (C14-18)-Si NW, i.e., the shorter the alkyl chain, the greater the Si-C binding energy. However, the oxidation resistance of the (C2-18)-Si NW25 is lower than for equivalent Si NW50 surfaces as explained and experimentally substantiated based on electronic (XPS and KP) and structure (TEM and HAADF) measurements
Beschreibung:Date Completed 21.05.2015
Date Revised 03.03.2015
published: Print-Electronic
Citation Status PubMed-not-MEDLINE
ISSN:1520-5827
DOI:10.1021/la5047244