Selective insertion of sulfur dioxide reduction intermediates on graphene oxide
Graphite microparticles (d50 6.20 μm) were oxidized by strong acids, and the resultant graphite oxide was thermally exfoliated to graphene oxide sheets (MPGO, C/O 1.53). Graphene oxide was treated with nonthermal plasma under a SO2 atmosphere at room temperature. The XPS spectrum showed that SO2 was...
Ausführliche Beschreibung
Bibliographische Detailangaben
| Veröffentlicht in: | Langmuir : the ACS journal of surfaces and colloids. - 1999. - 30(2014), 15 vom: 22. Apr., Seite 4301-9
|
|---|
| 1. Verfasser: |
Humeres, Eduardo
(VerfasserIn) |
|---|
| Weitere Verfasser: |
Debacher, Nito A,
Smaniotto, Alessandra,
de Castro, Karen M,
Benetoli, Luís O B,
de Souza, Eduardo P,
Moreira, Regina de F P M,
Lopes, Cristiane N,
Schreiner, Wido H,
Canle, Moisés,
Santaballa, J Arturo |
|---|
| Format: | Online-Aufsatz
|
|---|
| Sprache: | English |
|---|
| Veröffentlicht: |
2014
|
|---|
| Zugriff auf das übergeordnete Werk: | Langmuir : the ACS journal of surfaces and colloids
|
|---|
| Schlagworte: | Journal Article |
|---|