Fabrication of surface charge gradients in open-tubular capillaries and their characterization by spatially resolved pulsed streaming potential measurements
Surface charge gradients have been formed on the inside surface of 75 μm i.d. silica capillaries via controlled rate infusion using 3-aminopropyltriethoxysilane as the reactive precursor. These 400 mm length gradients have been characterized using spatially resolved streaming potential measurements,...
| Veröffentlicht in: | Langmuir : the ACS journal of surfaces and colloids. - 1992. - 29(2013), 49 vom: 10. Dez., Seite 15260-5 |
|---|---|
| 1. Verfasser: | |
| Weitere Verfasser: | , , , |
| Format: | Online-Aufsatz |
| Sprache: | English |
| Veröffentlicht: |
2013
|
| Zugriff auf das übergeordnete Werk: | Langmuir : the ACS journal of surfaces and colloids |
| Schlagworte: | Journal Article |
| Zusammenfassung: | Surface charge gradients have been formed on the inside surface of 75 μm i.d. silica capillaries via controlled rate infusion using 3-aminopropyltriethoxysilane as the reactive precursor. These 400 mm length gradients have been characterized using spatially resolved streaming potential measurements, from which the zeta potential as a function of distance was determined. The gradient capillaries exhibited a gradual variation in zeta potential from top to bottom, whereas uniformly modified and as-received capillaries were relatively homogeneous along their length. For a gradient prepared with a relatively high concentration of aminosilane, the zeta potential changed over 60 mV from one end of the capillary to the other, yielding a variation in the magnitude of the apparent surface charge of ~7 fold. By changing the concentration of the aminoalkoxysilane and/or the rate of infusion, both the value of the zeta potential (and hence surface charge) and its spatial profile (i.e., rate of change with distance) could be manipulated |
|---|---|
| Beschreibung: | Date Completed 24.07.2014 Date Revised 10.12.2013 published: Print-Electronic Citation Status PubMed-not-MEDLINE |
| ISSN: | 1520-5827 |
| DOI: | 10.1021/la402934m |