Multilayered composite microgels synthesized by surfactant-free seeded polymerization
We report on a simple and rapid method to produce multilayered composite microgels. Thermosensitive microgels were synthesized by aqueous free radical precipitation polymerization using N-isopropylacrylamide (NIPAm) as a monomer. Using the microgels as cores, surfactant-free seeded polymerization of...
| Veröffentlicht in: | Langmuir : the ACS journal of surfaces and colloids. - 1992. - 29(2013), 33 vom: 20. Aug., Seite 10579-85 |
|---|---|
| 1. Verfasser: | |
| Weitere Verfasser: | , |
| Format: | Online-Aufsatz |
| Sprache: | English |
| Veröffentlicht: |
2013
|
| Zugriff auf das übergeordnete Werk: | Langmuir : the ACS journal of surfaces and colloids |
| Schlagworte: | Journal Article |
| Zusammenfassung: | We report on a simple and rapid method to produce multilayered composite microgels. Thermosensitive microgels were synthesized by aqueous free radical precipitation polymerization using N-isopropylacrylamide (NIPAm) as a monomer. Using the microgels as cores, surfactant-free seeded polymerization of an oil-soluble monomer, glycidyl methacrylate (GMA), was carried out at 70 °C, where the microgels were highly deswollen in water. All of the oil-soluble monomers were polymerized, and the resultant polymers were attached on the pre-existing microgel cores, resulting in hard shell formation. It is worth mentioning that secondary particles of oil-soluble monomers have never been formed during the polymerization. The composite microgels were characterized by electron microscopy and dynamic light scattering. In particular, X-ray photoelectron spectroscopy (XPS) measurements revealed that the surface of the composite microgels was composed of a hydrogel layer, although microgel cores were covered by polyGMA shell. The mechanism of the trilayered composite microgel formation will be discussed |
|---|---|
| Beschreibung: | Date Completed 05.03.2014 Date Revised 20.08.2013 published: Print-Electronic Citation Status PubMed-not-MEDLINE |
| ISSN: | 1520-5827 |
| DOI: | 10.1021/la4025537 |