Water-soluble Pd nanoparticles capped with glutathione : synthesis, characterization, and magnetic properties
The synthesis, characterization, and magnetic properties of water-soluble Pd nanoparticles capped with glutathione are described. The glutathione-capped Pd nanoparticles were synthesized under argon and air atmospheres at room temperature. Whereas the former exhibits a bulklike lattice parameter, th...
| Veröffentlicht in: | Langmuir : the ACS journal of surfaces and colloids. - 1992. - 28(2012), 45 vom: 13. Nov., Seite 15958-65 |
|---|---|
| 1. Verfasser: | |
| Weitere Verfasser: | , |
| Format: | Online-Aufsatz |
| Sprache: | English |
| Veröffentlicht: |
2012
|
| Zugriff auf das übergeordnete Werk: | Langmuir : the ACS journal of surfaces and colloids |
| Schlagworte: | Journal Article Research Support, Non-U.S. Gov't Water 059QF0KO0R Palladium 5TWQ1V240M Glutathione GAN16C9B8O |
| Zusammenfassung: | The synthesis, characterization, and magnetic properties of water-soluble Pd nanoparticles capped with glutathione are described. The glutathione-capped Pd nanoparticles were synthesized under argon and air atmospheres at room temperature. Whereas the former exhibits a bulklike lattice parameter, the lattice parameter of the latter is found to be considerably greater, indicating anomalous lattice expansion. Comparative structural and compositional studies of these nanoparticles suggest the presence of oxygen in the core lattice when Pd nanoparticles are prepared under an air atmosphere. Both Pd nanoparticles prepared under argon and air show ferromagnetism at 5 K, but the latter exhibits significantly greater coercivity (88 Oe) and magnetization (0.09 emu/g at 50 kOe). The enhanced ferromagnetic properties are explained by the electronic effect of the incorporated oxygen that increases the 4d density of holes at the Pd site and localizes magnetic moments |
|---|---|
| Beschreibung: | Date Completed 19.04.2013 Date Revised 21.11.2013 published: Print-Electronic Citation Status MEDLINE |
| ISSN: | 1520-5827 |
| DOI: | 10.1021/la303326u |