Interactions of NO2 with amine-functionalized SBA-15 : effects of synthesis route
SBA-15 mesoporous silica was modified using (3-aminopropyl)trimethoxysilane (APTMS) following co-condensation or grafting methods and then used as a NO(2) adsorbent at room temperature. The samples were characterized before and after exposure to NO(2) by SEM-EDX, N(2) adsorption at 77 K, potentiomet...
| Veröffentlicht in: | Langmuir : the ACS journal of surfaces and colloids. - 1992. - 28(2012), 13 vom: 03. Apr., Seite 5703-14 |
|---|---|
| 1. Verfasser: | |
| Weitere Verfasser: | , |
| Format: | Online-Aufsatz |
| Sprache: | English |
| Veröffentlicht: |
2012
|
| Zugriff auf das übergeordnete Werk: | Langmuir : the ACS journal of surfaces and colloids |
| Schlagworte: | Journal Article |
| Zusammenfassung: | SBA-15 mesoporous silica was modified using (3-aminopropyl)trimethoxysilane (APTMS) following co-condensation or grafting methods and then used as a NO(2) adsorbent at room temperature. The samples were characterized before and after exposure to NO(2) by SEM-EDX, N(2) adsorption at 77 K, potentiometric titration, thermal analysis, and FTIR spectroscopy. Even though, regardless of the synthesis route, the addition of propylamine groups leads to a significant enhancement in the amount of NO(2) adsorbed (from 21 to 124 mg(NO(2))/g), a higher retention of NO(2) and NO (released as a result of surface reactions) was measured on the grafted silica than on all of the co-condensed samples. In the case of the latter materials, improvements in both NO(2) adsorption capacity and NO retention were found for the samples treated with NaOH. This behavior is related to the higher reactivity of deprotonated propylamine groups (formed during NaOH treatment) with NO(2), the presence of silanol groups, and the residual amount of sodium present in the samples. The mechanism of NO(2) adsorption on propylamine groups involves the formation of nitramine and/or nitrosamine. Analysis of the spent materials indicates that the porosity of co-condensed materials is not affected to the same extent by adsorption of NO(2) as that of the grafted silica |
|---|---|
| Beschreibung: | Date Completed 07.08.2012 Date Revised 03.04.2012 published: Print-Electronic Citation Status PubMed-not-MEDLINE |
| ISSN: | 1520-5827 |
| DOI: | 10.1021/la300371m |