Preparation, characterization and performance of a novel PVDF/PMMA/TPU blend hollow fiber membrane for wastewater treatment
Polyvinylidene fluoride (PVDF)/polymethylmethacrylate (PMMA)/thermoplastic polyurethane (TPU) blend hollow fiber membranes were successfully prepared by the wet-spinning method with the loading of PMMA and TPU in a range of polymer concentrations varying from 0 to 20 wt% and at a total polymer conce...
| Veröffentlicht in: | Water science and technology : a journal of the International Association on Water Pollution Research. - 1986. - 65(2012), 6 vom: 21., Seite 1041-7 |
|---|---|
| 1. Verfasser: | |
| Weitere Verfasser: | , |
| Format: | Online-Aufsatz |
| Sprache: | English |
| Veröffentlicht: |
2012
|
| Zugriff auf das übergeordnete Werk: | Water science and technology : a journal of the International Association on Water Pollution Research |
| Schlagworte: | Journal Article Research Support, Non-U.S. Gov't Membranes, Artificial Polyurethanes Polyvinyls polyvinylidene fluoride 24937-79-9 Polymethyl Methacrylate 9011-14-7 |
| Zusammenfassung: | Polyvinylidene fluoride (PVDF)/polymethylmethacrylate (PMMA)/thermoplastic polyurethane (TPU) blend hollow fiber membranes were successfully prepared by the wet-spinning method with the loading of PMMA and TPU in a range of polymer concentrations varying from 0 to 20 wt% and at a total polymer concentration of 16 wt%. The influence of the addition of PMMA and TPU on the morphologies and the properties of such prepared membranes was investigated through FTIR-ATR, SEM, viscosity measurements, UF experiments and mechanical strength tests. Based on the experimental results, the compatibility of the PVDF, PMMA and TPU blend was best under the conditions of the PVDF-rich phase. The elongation at break of the membrane increased to a maximum of 146% with increase in the TPU concentration to 20 wt% in dope solution. The addition of PMMA increased the water permeation flux from 120 to 195 L/(m(2) h) initially. The flux then decreased when PMMA concentration was increased to over 10 wt%. The membranes obtained at optimized blending ratio were applied to the dyeing process wastewater filtration. During continuous filtration for 8 h, the flux was stabilized at about 20 L/(m(2) h) at 0.1 MPa. The reduction in COD(Cr), turbidity and color were about 63, 84 and 63% respectively |
|---|---|
| Beschreibung: | Date Completed 03.05.2012 Date Revised 01.03.2012 published: Print Citation Status MEDLINE |
| ISSN: | 0273-1223 |
| DOI: | 10.2166/wst.2012.930 |