Role of Zr4+ cations in NO2 adsorption on Ce(1-x)Zr(x)O2 mixed oxides at ambient conditions
Mixed oxides Ce(1-x)Zr(x)O(2) prepared by slow coprecipitation in NaOH were tested for NO(2) adsorption in dynamic conditions at room temperature. The samples were characterized before and after exposure to NO(2) by XRD, N(2)-adsorption, thermal analysis, potentiometric titration, and FT-IR. Mixed o...
| Veröffentlicht in: | Langmuir : the ACS journal of surfaces and colloids. - 1992. - 27(2011), 15 vom: 02. Aug., Seite 9379-86 |
|---|---|
| 1. Verfasser: | |
| Weitere Verfasser: | , |
| Format: | Online-Aufsatz |
| Sprache: | English |
| Veröffentlicht: |
2011
|
| Zugriff auf das übergeordnete Werk: | Langmuir : the ACS journal of surfaces and colloids |
| Schlagworte: | Journal Article |
| Zusammenfassung: | Mixed oxides Ce(1-x)Zr(x)O(2) prepared by slow coprecipitation in NaOH were tested for NO(2) adsorption in dynamic conditions at room temperature. The samples were characterized before and after exposure to NO(2) by XRD, N(2)-adsorption, thermal analysis, potentiometric titration, and FT-IR. Mixed oxides show a better NO(2) adsorption capacity than the parent materials (CeO(2) and Zr(OH)(4)). This effect is linked to the presence of reduced cerium and oxygen vacancies induced by the addition of Zr(4+) cations to the structure. The results indicate that NO(2) reacts with Ce(3+) to form nitrite and nitrate species on the surface. The NO retention increases with an increase in the Zr(OH)(4) content. A decrease in the density of -OH groups on the surface after the exposure to NO(2), suggests their involvement in reactive adsorption of NO and/or NO(2). From the structural point of view, no real difference was observed on the Ce(1-x)Zr(x)O(2) materials before and after exposure to NO(2) |
|---|---|
| Beschreibung: | Date Completed 03.11.2011 Date Revised 26.07.2011 published: Print-Electronic Citation Status PubMed-not-MEDLINE |
| ISSN: | 1520-5827 |
| DOI: | 10.1021/la201338w |