Self-assembly of electrospun polymer nanofibers : a general phenomenon generating honeycomb-patterned nanofibrous structures
© 2011 American Chemical Society
| Veröffentlicht in: | Langmuir : the ACS journal of surfaces and colloids. - 1992. - 27(2011), 8 vom: 19. Apr., Seite 4285-9 |
|---|---|
| 1. Verfasser: | |
| Weitere Verfasser: | , , , , , |
| Format: | Online-Aufsatz |
| Sprache: | English |
| Veröffentlicht: |
2011
|
| Zugriff auf das übergeordnete Werk: | Langmuir : the ACS journal of surfaces and colloids |
| Schlagworte: | Journal Article |
| Zusammenfassung: | © 2011 American Chemical Society A general phenomenon that electrospun polymer nanofibers self-assemble into honeycomb-patterned nanofibrous structures (HNFSs) is reported. We used electrospinning to produce charged polymer nanofibers, which were kept in liquid state (wet) on landing on the substrates by appropriately controlling the electrospinning conditions. Driven by the competitive actions of surface tension and electrostatic repulsion, these charged wet nanofibers self-assemble into the HNFSs. Fabrication of the well-defined three-dimensional HNFSs was successfully demonstrated for three different polymers, that is, polyacrylonitrile, polyvinyl alcohol, and polyethylene oxide. The pore diameter of the obtained honeycomb structures spans a wide range from micrometers to over 200 μm with depths as large as over 150 μm. The pore walls are composed of uniaxially aligned polymer nanofibers |
|---|---|