Pattern-dependent tunable adhesion of superhydrophobic MnO2 nanostructured film
Tuning the adhesive force on a superhydrophobic MnO(2) nanostructured film was achieved by fabricating different patterns including meshlike, ball cactus-like, and tilted nanorod structures. The marvelous modulation range of the adhesive forces from 130 to nearly 0 μN endows these superhydrophobic s...
| Veröffentlicht in: | Langmuir : the ACS journal of surfaces and colloids. - 1992. - 27(2011), 7 vom: 05. Apr., Seite 3224-8 |
|---|---|
| 1. Verfasser: | |
| Weitere Verfasser: | , , , |
| Format: | Online-Aufsatz |
| Sprache: | English |
| Veröffentlicht: |
2011
|
| Zugriff auf das übergeordnete Werk: | Langmuir : the ACS journal of surfaces and colloids |
| Schlagworte: | Journal Article Research Support, Non-U.S. Gov't Manganese Compounds Oxides manganese oxide 64J2OA7MH3 |
| Zusammenfassung: | Tuning the adhesive force on a superhydrophobic MnO(2) nanostructured film was achieved by fabricating different patterns including meshlike, ball cactus-like, and tilted nanorod structures. The marvelous modulation range of the adhesive forces from 130 to nearly 0 μN endows these superhydrophobic surfaces with extraordinarily different dynamic properties of water droplets. This pattern-dependent adhesive property is attributed to the kinetic barrier difference resulting from the different continuity of the three-interface contact line. This finding will provide the general strategies for the adhesion adjustment on superhydrophobic surfaces |
|---|---|
| Beschreibung: | Date Completed 13.07.2011 Date Revised 25.11.2016 published: Print-Electronic Citation Status MEDLINE |
| ISSN: | 1520-5827 |
| DOI: | 10.1021/la104709d |