Virus-templated photoimprint on the surface of an azobenzene-containing polymer
A photoimprint-based immobilization process is presented for cylindrical viruses on the surface of an azobenzene-bearing acrylate polymer by using atomic force microscopy (AFM). Tobacco mosaic virus (TMV), 18 nm in diameter and ca. 300 nm in length, was employed as a model virus. First, a droplet of...
| Veröffentlicht in: | Langmuir : the ACS journal of surfaces and colloids. - 1992. - 26(2010), 15 vom: 03. Aug., Seite 12673-9 |
|---|---|
| 1. Verfasser: | |
| Weitere Verfasser: | , , , , , , , , |
| Format: | Online-Aufsatz |
| Sprache: | English |
| Veröffentlicht: |
2010
|
| Zugriff auf das übergeordnete Werk: | Langmuir : the ACS journal of surfaces and colloids |
| Schlagworte: | Journal Article Research Support, Non-U.S. Gov't Azo Compounds Polymers azobenzene F0U1H6UG5C |
| Zusammenfassung: | A photoimprint-based immobilization process is presented for cylindrical viruses on the surface of an azobenzene-bearing acrylate polymer by using atomic force microscopy (AFM). Tobacco mosaic virus (TMV), 18 nm in diameter and ca. 300 nm in length, was employed as a model virus. First, a droplet of an aqueous solution containing TMV was placed on the acrylate polymer surface. After drying the droplet, the polymer surface was irradiated with light at a wavelength of 470 nm from blue-light-emitting diodes. Finally, the surface was washed by aqueous solution with detergents. The polymer surface was observed at each step by AFM. TMV was shown to embed itself gradually on the polymer surface during photoirradiation in a time scale of tens of minutes because of the formation of the surface groove complementary to the shape of TMV. Analysis of immobilization efficiency of TMV on the polymer surface by the immunological enzyme luminescence indicated that efficiency increased proportional to the photoirradiation time. In these experimental conditions, the absorption band of the azobenzene moiety remained constant before and after the photoirradiation. These results show that TMV is physically held on the complementary groove formed on the polymer surface by the photoirradiation |
|---|---|
| Beschreibung: | Date Completed 04.11.2010 Date Revised 15.11.2012 published: Print Citation Status MEDLINE |
| ISSN: | 1520-5827 |
| DOI: | 10.1021/la101229p |