Self-structured surface patterns on molecular azo glass films induced by laser light irradiation
In this work, formation of photoinduced self-structured surface pattern and its correlation with chromophoric structures were studied by using a series of star-shaped azo compounds, which exist as stable molecular glass at room temperature. For the synthesis, a star-shaped precursor (Tr-AN) was prep...
| Veröffentlicht in: | Langmuir : the ACS journal of surfaces and colloids. - 1992. - 26(2010), 9 vom: 04. Mai, Seite 6755-61 |
|---|---|
| 1. Verfasser: | |
| Weitere Verfasser: | , |
| Format: | Online-Aufsatz |
| Sprache: | English |
| Veröffentlicht: |
2010
|
| Zugriff auf das übergeordnete Werk: | Langmuir : the ACS journal of surfaces and colloids |
| Schlagworte: | Journal Article |
| Zusammenfassung: | In this work, formation of photoinduced self-structured surface pattern and its correlation with chromophoric structures were studied by using a series of star-shaped azo compounds, which exist as stable molecular glass at room temperature. For the synthesis, a star-shaped precursor (Tr-AN) was prepared by a ring-open reaction between 1, 3, 5-triglycidyl isocyanurate and N-methylaniline. The star-shaped azo compounds were then synthesized through azo-coupling reactions between the precursor and diazonium salts of 4-nitroaniline, 2-methyl-4-nitroaniline, and 4-aminobenzonitrile, respectively. Through these steps, three azo compounds were obtained to bear different donor-acceptor type azo chromophores at the peripheral positions. The formation of the photoinduced self-structured patterns was investigated by irradiating solid thin films of the molecular azo glass with a uniform laser beam (532 nm, 200 mW/cm(2)) at normal incidence. For comparison, formation of surface-relief-gratings (SRGs) was also investigated by exposing the thin films to an interference pattern of the laser beams (532 nm, 80 mW/cm(2)). The results show that SRGs can be inscribed on the films of all three star-shaped azo compounds, but self-structured surface patterns is only observed on film of the azo compound containing 4-cyanoazobenzene moieties (Tr-AZ-CN) under the same irradiation condition. The electron-withdrawing groups, which control the absorption band position, show a significant influence on both the self-structured pattern formation and SRG inscription rate. Under proper experimental conditions, both self-structured surface pattern and SRG can simultaneously be observed on the Tr-AZ-CN films. The observations can lead to a deeper understanding of the photoinduced effects, especially their correlation with molecular structures |
|---|---|
| Beschreibung: | Date Completed 02.08.2010 Date Revised 27.04.2010 published: Print Citation Status PubMed-not-MEDLINE |
| ISSN: | 1520-5827 |
| DOI: | 10.1021/la9041056 |