Iron-induced cyclodextrin self-assembly into size-controllable nanospheres
Iron-induced self-assembly of beta-cyclodextrin, beta-CD, into size controllable nanospheres with a well-defined spherical morphology and a relatively narrow size distribution was formed when acetone was added to a solution of beta-CD with iron(II) acetate, Fe(OAc)(2), in DMF. Thermogravimetric anal...
| Veröffentlicht in: | Langmuir : the ACS journal of surfaces and colloids. - 1992. - 26(2010), 4 vom: 16. Feb., Seite 2418-23 |
|---|---|
| 1. Verfasser: | |
| Weitere Verfasser: | |
| Format: | Online-Aufsatz |
| Sprache: | English |
| Veröffentlicht: |
2010
|
| Zugriff auf das übergeordnete Werk: | Langmuir : the ACS journal of surfaces and colloids |
| Schlagworte: | Journal Article Research Support, Non-U.S. Gov't Ferric Compounds beta-Cyclodextrins ferric acetate CZZ8832SI5 betadex JV039JZZ3A |
| Zusammenfassung: | Iron-induced self-assembly of beta-cyclodextrin, beta-CD, into size controllable nanospheres with a well-defined spherical morphology and a relatively narrow size distribution was formed when acetone was added to a solution of beta-CD with iron(II) acetate, Fe(OAc)(2), in DMF. Thermogravimetric analysis, inductively coupled plasma atomic emission spectroscopy, and high resolution transmission electron microscopy showed that the irons were present as a well-dispersed state in the beta-CD nanospheres. In the (1)H NMR spectrum of the beta-CD/Fe(OAc)(2), beta/Fe, solution before adding acetone, the peaks corresponding to beta-CD were broadened and their spin-spin splitting had disappeared. In particular, the beta/Fe solutions were found to remain in a clean solution state at 1 week after solution preparation. These findings indicate the isolation of individual iron ions caused by the surrounding of each ion with the beta-CD molecules in the solution before the addition of acetone. X-ray crystal structure analysis, morphological observations, and N(2) adsorption and desorption experiments showed that the beta-CD nanospheres were generated by the formation of iron-embedded beta-CD primary particles with disordered cage type structure and simultaneous spherical assembly of the primary particles during the addition of acetone to the beta/Fe solution with appropriate mole ratio between beta-CD and Fe(OAc)(2). Interestingly, the size of the beta-CD nanospheres could be simply controlled by changing the speed at which acetone was added to the solution, with higher acetone addition speeds yielding smaller particles |
|---|---|
| Beschreibung: | Date Completed 26.04.2010 Date Revised 15.11.2012 published: Print Citation Status MEDLINE |
| ISSN: | 1520-5827 |
| DOI: | 10.1021/la9028645 |