Pd-supported catalysts : evolution of support porous texture along Pd deposition and alkali-metal doping

Adsorption of N2 at 77 K and scanning electron microscopy have been used to measure the changes in the support morphology, at nano- and microscale level, along the processes involved in the preparation of a supported Pd catalyst: Pd deposition, doping, and thermal treatments. Among the investigated...

Ausführliche Beschreibung

Bibliographische Detailangaben
Veröffentlicht in:Langmuir : the ACS journal of surfaces and colloids. - 1992. - 25(2009), 11 vom: 02. Juni, Seite 6476-85
1. Verfasser: Pellegrini, R (VerfasserIn)
Weitere Verfasser: Leofanti, G, Agostini, G, Groppo, E, Rivallan, M, Lamberti, C
Format: Online-Aufsatz
Sprache:English
Veröffentlicht: 2009
Zugriff auf das übergeordnete Werk:Langmuir : the ACS journal of surfaces and colloids
Schlagworte:Journal Article
LEADER 01000naa a22002652 4500
001 NLM187663610
003 DE-627
005 20231223180501.0
007 cr uuu---uuuuu
008 231223s2009 xx |||||o 00| ||eng c
024 7 |a 10.1021/la900084p  |2 doi 
028 5 2 |a pubmed24n0626.xml 
035 |a (DE-627)NLM187663610 
035 |a (NLM)19348495 
040 |a DE-627  |b ger  |c DE-627  |e rakwb 
041 |a eng 
100 1 |a Pellegrini, R  |e verfasserin  |4 aut 
245 1 0 |a Pd-supported catalysts  |b evolution of support porous texture along Pd deposition and alkali-metal doping 
264 1 |c 2009 
336 |a Text  |b txt  |2 rdacontent 
337 |a ƒaComputermedien  |b c  |2 rdamedia 
338 |a ƒa Online-Ressource  |b cr  |2 rdacarrier 
500 |a Date Completed 25.08.2009 
500 |a Date Revised 26.05.2009 
500 |a published: Print 
500 |a Citation Status PubMed-not-MEDLINE 
520 |a Adsorption of N2 at 77 K and scanning electron microscopy have been used to measure the changes in the support morphology, at nano- and microscale level, along the processes involved in the preparation of a supported Pd catalyst: Pd deposition, doping, and thermal treatments. Among the investigated supports, viz., activated carbons, gamma-Al2O3, SiO2, and SiO2-Al2O3 (SA), the SA one was found particularly sensitive to these processes, as a result of its high plasticity and reactivity. Involved processes can be summarized as follows: (i) During the Pd deposition, the support itself is partially dissolved and removed as a result of both the basicity of the precipitating agent and the final washing. (ii) When the undoped sample is thermally treated up to 823 K, only modest phenomena are observed. (iii) Upon doping with potassium carbonate, the support dissolution continues, and the greater the carbonate concentration, the greater the dissolution extent. In this case the dissolved material is not removed, but reprecipitates (partially outside the pores), during the subsequent drying at 393 K. (iv) When doped samples are thermally treated, the reaction between carbonate and support causes the mobilization of the support itself, with sintering phenomena that can reach the total collapse of the porous structure. The starting temperature of the pore collapse decreases with increasing potassium carbonate concentration. The modification of the support influences, directly or indirectly, the surface properties and the availability of Pd particles that can be doped or even covered by materials from support and made more or less accessible or even inaccessible by pore narrowing, widening, or blocking 
650 4 |a Journal Article 
700 1 |a Leofanti, G  |e verfasserin  |4 aut 
700 1 |a Agostini, G  |e verfasserin  |4 aut 
700 1 |a Groppo, E  |e verfasserin  |4 aut 
700 1 |a Rivallan, M  |e verfasserin  |4 aut 
700 1 |a Lamberti, C  |e verfasserin  |4 aut 
773 0 8 |i Enthalten in  |t Langmuir : the ACS journal of surfaces and colloids  |d 1992  |g 25(2009), 11 vom: 02. Juni, Seite 6476-85  |w (DE-627)NLM098181009  |x 1520-5827  |7 nnns 
773 1 8 |g volume:25  |g year:2009  |g number:11  |g day:02  |g month:06  |g pages:6476-85 
856 4 0 |u http://dx.doi.org/10.1021/la900084p  |3 Volltext 
912 |a GBV_USEFLAG_A 
912 |a SYSFLAG_A 
912 |a GBV_NLM 
912 |a GBV_ILN_22 
912 |a GBV_ILN_350 
912 |a GBV_ILN_721 
951 |a AR 
952 |d 25  |j 2009  |e 11  |b 02  |c 06  |h 6476-85