Temperature stability of the interfacial structure between a sulfonated crystalline alkyl side-chain polymer and a soft adhesive

The fracture toughness of interfaces between a sulfonated alkyl side-chain graft copolymer and a soft acrylic random copolymer containing acrylic acid monomers was investigated with a probe test method. Interfaces between a thin (100 nm) layer of the block copolymer and a thick (100 microm) layer of...

Ausführliche Beschreibung

Bibliographische Detailangaben
Veröffentlicht in:Langmuir : the ACS journal of surfaces and colloids. - 1992. - 24(2008), 18 vom: 16. Sept., Seite 10169-73
1. Verfasser: Retsos, Haris (VerfasserIn)
Weitere Verfasser: Lee, Daewon, Lim, Min-Young, Lee, Jong-Chan, Char, Kookheon, Creton, Costantino
Format: Online-Aufsatz
Sprache:English
Veröffentlicht: 2008
Zugriff auf das übergeordnete Werk:Langmuir : the ACS journal of surfaces and colloids
Schlagworte:Journal Article
LEADER 01000naa a22002652 4500
001 NLM181563274
003 DE-627
005 20231223161450.0
007 cr uuu---uuuuu
008 231223s2008 xx |||||o 00| ||eng c
024 7 |a 10.1021/la801043r  |2 doi 
028 5 2 |a pubmed24n0605.xml 
035 |a (DE-627)NLM181563274 
035 |a (NLM)18700749 
040 |a DE-627  |b ger  |c DE-627  |e rakwb 
041 |a eng 
100 1 |a Retsos, Haris  |e verfasserin  |4 aut 
245 1 0 |a Temperature stability of the interfacial structure between a sulfonated crystalline alkyl side-chain polymer and a soft adhesive 
264 1 |c 2008 
336 |a Text  |b txt  |2 rdacontent 
337 |a ƒaComputermedien  |b c  |2 rdamedia 
338 |a ƒa Online-Ressource  |b cr  |2 rdacarrier 
500 |a Date Completed 17.10.2008 
500 |a Date Revised 10.09.2008 
500 |a published: Print-Electronic 
500 |a Citation Status PubMed-not-MEDLINE 
520 |a The fracture toughness of interfaces between a sulfonated alkyl side-chain graft copolymer and a soft acrylic random copolymer containing acrylic acid monomers was investigated with a probe test method. Interfaces between a thin (100 nm) layer of the block copolymer and a thick (100 microm) layer of the acrylic copolymer were prepared at room temperature and subsequently annealed for 7 h at different temperatures. After the annealing step, the interface was quenched to room temperature and tested, a strategy that provides the advantage of keeping constant the mechanical properties of the materials on both sides of the interface so that any major difference in adhesive behavior can only be attributed to a change in the interfacial structure. For annealing temperatures below the crystalline to liquid crystalline transition temperature (86 degrees C), the adhesion energy remained very low and failure occurred by interfacial crack propagation. However when the interface was annealed above that temperature, a much higher adhesion energy was observed at room temperature because of the formation of a fibrillar structure upon debonding. The results indicate that the crystalline order at low temperature is very stable presumably because of the strong interactions between the sulfone groups in the side chains. However, when these interactions weaken and the side chains become liquid crystalline, the surface reconstruction mechanism cannot be prevented and strong interactions formed between the polar parts of the copolymer and the acrylic acid. These strong interactions remain during the cooling step, and a mechanism of surface reconstruction is proposed 
650 4 |a Journal Article 
700 1 |a Lee, Daewon  |e verfasserin  |4 aut 
700 1 |a Lim, Min-Young  |e verfasserin  |4 aut 
700 1 |a Lee, Jong-Chan  |e verfasserin  |4 aut 
700 1 |a Char, Kookheon  |e verfasserin  |4 aut 
700 1 |a Creton, Costantino  |e verfasserin  |4 aut 
773 0 8 |i Enthalten in  |t Langmuir : the ACS journal of surfaces and colloids  |d 1992  |g 24(2008), 18 vom: 16. Sept., Seite 10169-73  |w (DE-627)NLM098181009  |x 1520-5827  |7 nnns 
773 1 8 |g volume:24  |g year:2008  |g number:18  |g day:16  |g month:09  |g pages:10169-73 
856 4 0 |u http://dx.doi.org/10.1021/la801043r  |3 Volltext 
912 |a GBV_USEFLAG_A 
912 |a SYSFLAG_A 
912 |a GBV_NLM 
912 |a GBV_ILN_22 
912 |a GBV_ILN_350 
912 |a GBV_ILN_721 
951 |a AR 
952 |d 24  |j 2008  |e 18  |b 16  |c 09  |h 10169-73