Preparation of activated ordered mesoporous carbons with a channel structure
Activated ordered mesoporous carbons with a channel structure (AOMCs-CS) were successfully prepared by imposing CO(2) activation on ordered mesopore carbon C-FDU-15. It is found that the continuous carbon framework of the precursor C-FDU-15 plays an important role in keeping the order structure of t...
| Veröffentlicht in: | Langmuir : the ACS journal of surfaces and colloids. - 1992. - 24(2008), 7 vom: 01. Apr., Seite 2967-9 |
|---|---|
| 1. Verfasser: | |
| Weitere Verfasser: | , , , , , , |
| Format: | Online-Aufsatz |
| Sprache: | English |
| Veröffentlicht: |
2008
|
| Zugriff auf das übergeordnete Werk: | Langmuir : the ACS journal of surfaces and colloids |
| Schlagworte: | Journal Article |
| Zusammenfassung: | Activated ordered mesoporous carbons with a channel structure (AOMCs-CS) were successfully prepared by imposing CO(2) activation on ordered mesopore carbon C-FDU-15. It is found that the continuous carbon framework of the precursor C-FDU-15 plays an important role in keeping the order structure of the resulting AOMCs-CS. The mild activation (e.g., 31 wt % burnoff) does not impair the order degree. After that, the order degree gradually decreases with further increasing burnoff. However, the basic hexagonal mesostructure of C-FDU-15 can still be found in the AOMCs-CS when the burnoff is up to 73 wt %, although many carbon walls are punched and thus many larger mesopores and marcropores are generated. With increasing burnoff, the surface area and volume of micropores increase first and then decrease, and the surface area and volume of mesopores continuously increase. The highest measured Brunaruer-Emmett-Teller (BET) surface area, micropore volume, and total pore volume of the AOMCs-CS reach 2004 m(2)/g, 0.50 cm(3)/g, and 1.22 cm(3)/g, respectively |
|---|---|
| Beschreibung: | Date Completed 05.05.2008 Date Revised 26.03.2008 published: Print-Electronic Citation Status PubMed-not-MEDLINE |
| ISSN: | 1520-5827 |
| DOI: | 10.1021/la703511z |