Revisiting the morphology development of solvent-swollen composite polymer particles at thermodynamic equilibrium
Morphology of polystyrene (PS)/poly(methyl methacrylate) (PMMA)/toluene droplets, in which phase separation proceeds, dispersed in SDS aqueous solution was examined. It changed from ex-centered PS-core/PMMA-shell to hemisphere with increasing SDS concentration. At low polymer weight fraction (wp), P...
| Veröffentlicht in: | Langmuir : the ACS journal of surfaces and colloids. - 1985. - 23(2007), 11 vom: 22. Mai, Seite 5914-9 |
|---|---|
| 1. Verfasser: | |
| Weitere Verfasser: | , |
| Format: | Aufsatz |
| Sprache: | English |
| Veröffentlicht: |
2007
|
| Zugriff auf das übergeordnete Werk: | Langmuir : the ACS journal of surfaces and colloids |
| Schlagworte: | Journal Article |
| Zusammenfassung: | Morphology of polystyrene (PS)/poly(methyl methacrylate) (PMMA)/toluene droplets, in which phase separation proceeds, dispersed in SDS aqueous solution was examined. It changed from ex-centered PS-core/PMMA-shell to hemisphere with increasing SDS concentration. At low polymer weight fraction (wp), PS and PMMA phases contained non-negligible amount of PMMA and PS, respectively. The small amount of PS and PMMA in PMMA and PS phases, respectively, affected significantly the interfacial tension between polymer/toluene and aqueous solutions. Interfacial tension between PS and PMMA phases at low wp was measured by the spinning drop method, showing a quite low value ( approximately 10-2 mN/m). Predicted morphology obtained from calculation of minimum total interfacial free energy of the droplets using the interfacial tensions agreed well with the experimental observation |
|---|---|
| Beschreibung: | Date Completed 11.07.2007 Date Revised 15.05.2007 published: Print-Electronic Citation Status PubMed-not-MEDLINE |
| ISSN: | 1520-5827 |