Humidity-sensitive electrical conductivity of a Langmuir-Blodgett film of titania nanosheets : surface modification as induced by light irradiation under humid conditions
Electrical conductivity of titania nanosheets was investigated for a single-layered Langmuir-Blodgett (LB) film deposited onto a comb-type electrode (5 or 10 microm (electrode spacing) x 8 mm (electrode width)). The photoresponsive electrical properties of the film were investigated by irradiating w...
| Veröffentlicht in: | Langmuir : the ACS journal of surfaces and colloids. - 1992. - 22(2006), 24 vom: 21. Nov., Seite 10066-71 |
|---|---|
| 1. Verfasser: | |
| Weitere Verfasser: | , , , , , , , |
| Format: | Aufsatz |
| Sprache: | English |
| Veröffentlicht: |
2006
|
| Zugriff auf das übergeordnete Werk: | Langmuir : the ACS journal of surfaces and colloids |
| Schlagworte: | Journal Article |
| Zusammenfassung: | Electrical conductivity of titania nanosheets was investigated for a single-layered Langmuir-Blodgett (LB) film deposited onto a comb-type electrode (5 or 10 microm (electrode spacing) x 8 mm (electrode width)). The photoresponsive electrical properties of the film were investigated by irradiating with a Xe lamp under various atmospheric conditions. The atmosphere was controlled by introducing either oxygen or nitrogen gases containing different amounts of water vapor. As a result, the LB film behaved as an insulator with little photoresponse under dry atmospheric conditions. It became conductive on illuminating with a Xe lamp under a wet oxygen atmosphere. Conductivity increased with the increase of irradiation time (0-30 min) to attain a stationary value in 1 h. The highest conductive state thus attained lasted for several hours in the dark. The impedance of the film was measured over the frequency range of 1 MHz to 50 Hz by varying the relative humidity of an atmosphere from 0 to 100%. The results were analyzed by assuming an equivalent circuit consisting of one resistance (R) with constant Warburg component (W) and one capacitance (C) in parallel. The R component depended remarkably on the relative humidity, while the C component stayed nearly at the constant value. The dependence of R on water vapor (PH2O) was expressed by R = A[PH2O]n with A = constant and n = -2.9. The results were rationalized in terms of the surface modification of titania nanosheets to hydrophilic nature under the illumination of UV light |
|---|---|
| Beschreibung: | Date Completed 13.03.2007 Date Revised 19.11.2006 published: Print Citation Status PubMed-not-MEDLINE |
| ISSN: | 1520-5827 |