Synthesis of ordered mesoporous zirconium phosphate films by spin coating and vapor treatments
Ordered mesoporous zirconium phosphate films were prepared on a silicon substrate by spin coating using a mixture of zirconium isopropoxide, triethyl phosphate, Pluronic P123 triblock copolymer, nitric acid, ethanol, and water. The spin-on film was consecutively treated with vapors of phosphoric aci...
| Veröffentlicht in: | Langmuir : the ACS journal of surfaces and colloids. - 1991. - 22(2006), 23 vom: 07. Nov., Seite 9469-72 |
|---|---|
| 1. Verfasser: | |
| Weitere Verfasser: | , , , , |
| Format: | Aufsatz |
| Sprache: | English |
| Veröffentlicht: |
2006
|
| Zugriff auf das übergeordnete Werk: | Langmuir : the ACS journal of surfaces and colloids |
| Schlagworte: | Journal Article |
| Zusammenfassung: | Ordered mesoporous zirconium phosphate films were prepared on a silicon substrate by spin coating using a mixture of zirconium isopropoxide, triethyl phosphate, Pluronic P123 triblock copolymer, nitric acid, ethanol, and water. The spin-on film was consecutively treated with vapors of phosphoric acid and ammonia. The post-vapor treatments effectively enhanced the thermal stability of an ordered mesostructure when heated to 500 degrees C. XRD and TEM analyses show that the calcined zirconium phosphate film has a hexagonal structure with straight channels parallel to the film surface. The zirconium phosphate film exhibited high proton conductivity of 0.02 S/cm parallel to the film surface at 80% RH and 25 degrees C |
|---|---|
| Beschreibung: | Date Completed 07.09.2007 Date Revised 31.10.2006 published: Print Citation Status PubMed-not-MEDLINE |
| ISSN: | 0743-7463 |