Electrochemical synthesis of a polypyrrole thin film with supercritical carbon dioxide as a solvent
A conductive polypyrrole (PPy) film was successfully synthesized in a homogeneous supercritical carbon dioxide (scCO2)/acetonitrile (AN) system. The occurrence of a homogeneous supercritical state was confirmed by observations of the phase behavior of the system through a high-pressure cell with a v...
| Veröffentlicht in: | Langmuir : the ACS journal of surfaces and colloids. - 1992. - 21(2005), 26 vom: 20. Dez., Seite 12303-8 |
|---|---|
| 1. Verfasser: | |
| Weitere Verfasser: | , , , , , |
| Format: | Aufsatz |
| Sprache: | English |
| Veröffentlicht: |
2005
|
| Zugriff auf das übergeordnete Werk: | Langmuir : the ACS journal of surfaces and colloids |
| Schlagworte: | Journal Article |
| Zusammenfassung: | A conductive polypyrrole (PPy) film was successfully synthesized in a homogeneous supercritical carbon dioxide (scCO2)/acetonitrile (AN) system. The occurrence of a homogeneous supercritical state was confirmed by observations of the phase behavior of the system through a high-pressure cell with a viewing window. The concentration of a supporting electrolyte, tetrabutylammonium hexafluorophosphate (TBAPF6), significantly changed the phase behavior of the scCO2/AN system. The polymerization rate of the film in that system decreased with further addition of CO2. This result suggested that the low viscosity of scCO2 did not play an important role in improving the growth rate of the PPy film. The low polymerization rate might have been due to the electron-transfer resistance arising from the low dielectric constant of scCO2/AN mixture. The roughness of the film prepared in the homogeneous scCO2/AN system was 1/10 that synthesized in AN itself as a solvent. The slow growth of film and the high diffusion rate of the monomer seemed to account for the smooth flat film formation |
|---|---|
| Beschreibung: | Date Completed 19.07.2007 Date Revised 13.12.2005 published: Print Citation Status PubMed-not-MEDLINE |
| ISSN: | 1520-5827 |