Fe3O4-LiMo3Se3 nanoparticle clusters as superparamagnetic nanocompasses
A scaleable chemical approach to functional nanoscale analogues of the magnetic compasses in magnetotactic bacteria is described. LiMo(3)Se(3)-Fe(3)O(4) nanowire-nanoparticle composites were synthesized by a reaction of 3-iodopropionic acid treated LiMo(3)Se(3) nanowire bundles with oleic acid-stabi...
| Veröffentlicht in: | Langmuir : the ACS journal of surfaces and colloids. - 1992. - 21(2005), 21 vom: 11. Okt., Seite 9709-13 |
|---|---|
| 1. Verfasser: | |
| Weitere Verfasser: | , , |
| Format: | Aufsatz |
| Sprache: | English |
| Veröffentlicht: |
2005
|
| Zugriff auf das übergeordnete Werk: | Langmuir : the ACS journal of surfaces and colloids |
| Schlagworte: | Journal Article |
| Zusammenfassung: | A scaleable chemical approach to functional nanoscale analogues of the magnetic compasses in magnetotactic bacteria is described. LiMo(3)Se(3)-Fe(3)O(4) nanowire-nanoparticle composites were synthesized by a reaction of 3-iodopropionic acid treated LiMo(3)Se(3) nanowire bundles with oleic acid-stabilized Fe(3)O(4) nanoparticles of 2.8, 5.3, and 12.5 nm size in tetrahydrofuran. Transmission electron micrographs show that the composite consists of Fe(3)O(4) nanoparticles attached to the surfaces of the 4-6 nm thick nanowire bundles. UV/vis spectra reveal absorptions from the nanowire (506 nm) and magnetite components (280-450 nm), and IR spectra show characteristic bands for the propionic acid linkers and for the residual oleic acid ligands on the magnetite particles. In the presence of excess oleic acid, the nanocomposites undergo rapid disassembly, suggesting that Fe(3)O(4) nanoparticles are bonded to nanowires via carboxylate groups from the linkers. Ultrasonication of a dispersion of the composite in THF produces individual LiMo(3)Se(3)-Fe(3)O(4) clusters, which are 340 +/- 107 nm long and 20 +/- 5 nm thick, depending on the sonication time and Fe(3)O(4) nanoparticle size. Field cooled and zero-field cooled magnetization measurements reveal that the blocking temperature (T(B) = 100 K) of the clusters with 5.3 nm Fe(3)O(4) is increased as compared to the free nanoparticles (T(B) = 30 K). Directional dipolar interactions in the clusters lead to magnetic anisotropy, which makes it possible to align the clusters in a magnetic field (900 Oe) |
|---|---|
| Beschreibung: | Date Completed 10.04.2007 Date Revised 06.10.2005 published: Print Citation Status PubMed-not-MEDLINE |
| ISSN: | 1520-5827 |