Electron beam irradiation of poly(vinyl methyl ether) films : 1. Synthesis and film topography
Temperature-sensitive hydrogel layers on silicon (Si) substrates were synthesized by electron beam irradiation of spin-coated poly(vinyl methyl ether) (PVME) films. The influences of the used solvent, the polymer concentration, and the spinning velocity on the homogeneity and the thickness of the PV...
| Veröffentlicht in: | Langmuir : the ACS journal of surfaces and colloids. - 1992. - 21(2005), 13 vom: 21. Juni, Seite 6073-80 |
|---|---|
| 1. Verfasser: | |
| Weitere Verfasser: | , , , , , |
| Format: | Aufsatz |
| Sprache: | English |
| Veröffentlicht: |
2005
|
| Zugriff auf das übergeordnete Werk: | Langmuir : the ACS journal of surfaces and colloids |
| Schlagworte: | Journal Article |
| Zusammenfassung: | Temperature-sensitive hydrogel layers on silicon (Si) substrates were synthesized by electron beam irradiation of spin-coated poly(vinyl methyl ether) (PVME) films. The influences of the used solvent, the polymer concentration, and the spinning velocity on the homogeneity and the thickness of the PVME film were investigated. In the range of concentration c(p) = 1-15 wt% PVME in ethanol solution, homogeneous films with a thickness between d = 50 nm and 1.7 mum were obtained. The films were cross-linked by electron beam irradiation under inert atmosphere and analyzed by sol-gel-analysis. The results were compared with bulkgels formed by electron beam irradiation of PVME in the dry state. The film topography was analyzed by high-resolution field emission scanning electron microscopy and atomic force microscopy. An islandlike structure in the dry, swollen, and shrunken state of the hydrogel films was observed |
|---|---|
| Beschreibung: | Date Completed 23.06.2006 Date Revised 14.06.2005 published: Print Citation Status PubMed-not-MEDLINE |
| ISSN: | 1520-5827 |