Electrospun poly(styrene-block-dimethylsiloxane) block copolymer fibers exhibiting superhydrophobicity
Block copolymer poly(styrene-b-dimethylsiloxane) fibers with submicrometer diameters in the range 150-400 nm were produced by electrospinning from solution in tetrahydrofuran and dimethylformamide. Contact angle measurements indicate that the nonwoven fibrous mats are superhydrophobic, with a contac...
| Veröffentlicht in: | Langmuir : the ACS journal of surfaces and colloids. - 1985. - 21(2005), 12 vom: 07. Juni, Seite 5549-54 |
|---|---|
| 1. Verfasser: | |
| Weitere Verfasser: | , , , |
| Format: | Aufsatz |
| Sprache: | English |
| Veröffentlicht: |
2005
|
| Zugriff auf das übergeordnete Werk: | Langmuir : the ACS journal of surfaces and colloids |
| Schlagworte: | Journal Article |
| Zusammenfassung: | Block copolymer poly(styrene-b-dimethylsiloxane) fibers with submicrometer diameters in the range 150-400 nm were produced by electrospinning from solution in tetrahydrofuran and dimethylformamide. Contact angle measurements indicate that the nonwoven fibrous mats are superhydrophobic, with a contact angle of 163 degrees and contact angle hysteresis of 15 degrees . The superhydrophobicity is attributed to the combined effects of surface enrichment in siloxane as revealed by X-ray photoelectron spectroscopy and surface roughness of the electrospun mat itself. Additionally, the fibers are shown by transmission electron microscopy to exhibit microphase-separated internal structures. Calorimetric studies confirm the strong segregation between the polystyrene and poly(dimethylsiloxane) blocks |
|---|---|
| Beschreibung: | Date Completed 28.07.2006 Date Revised 31.05.2005 published: Print Citation Status PubMed-not-MEDLINE |
| ISSN: | 1520-5827 |