Control of surface properties using fluorinated polymer brushes produced by surface-initiated controlled radical polymerization
Surface-grafted styrene-based homopolymer and diblock copolymer brushes bearing semifluorinated alkyl side groups were synthesized by nitroxide-mediated controlled radical polymerization on planar silicon oxide surfaces. The polymer brushes were characterized by X-ray photoelectron spectroscopy (XPS...
| Veröffentlicht in: | Langmuir : the ACS journal of surfaces and colloids. - 1985. - 20(2004), 24 vom: 23. Nov., Seite 10498-506 |
|---|---|
| 1. Verfasser: | |
| Weitere Verfasser: | , , , , , , |
| Format: | Aufsatz |
| Sprache: | English |
| Veröffentlicht: |
2004
|
| Zugriff auf das übergeordnete Werk: | Langmuir : the ACS journal of surfaces and colloids |
| Schlagworte: | Journal Article Research Support, U.S. Gov't, Non-P.H.S. Fluorocarbon Polymers Styrene 44LJ2U959V Silicon Dioxide 7631-86-9 |
| Zusammenfassung: | Surface-grafted styrene-based homopolymer and diblock copolymer brushes bearing semifluorinated alkyl side groups were synthesized by nitroxide-mediated controlled radical polymerization on planar silicon oxide surfaces. The polymer brushes were characterized by X-ray photoelectron spectroscopy (XPS), near-edge X-ray absorption fine structure (NEXAFS), and time-dependent water contact angle measurements. Angle-resolved XPS studies and water contact angle measurements showed that, in the case of the diblock copolymer brushes, the second block to be added was always exposed at the polymer-air interface regardless of its surface energy. Values of z*/Rg were estimated based on the radius of gyration, Rg, of the grafted homopolymer or block copolymer chains for the grafted brushes and thickness of the brush, z*. The fact that z*/Rg > 1 suggests that all these brushes are stretched. These results support the idea that after grafting the first block onto the surface the nitroxide-end capped polymer chains were able to polymerize the second block in a "living" fashion and the stretched brush so formed was dense enough that the outermost block in all cases completely covers the surface. NEXAFS analysis showed a relationship between the surface orientation of the fluorinated side chains and brush thickness with thicker brushes having more oriented side chains. Time-dependent water contact angle measurements revealed that the orientation of the side chains of the brush improved the surface stability toward reconstruction upon prolonged exposure to water |
|---|---|