Thermo-reversible swelling of thin hydrogel films immobilized by low-pressure plasma
Thin films of graft copolymers consisting of poly(N-isopropylacrylamide) (PNiPAAm) or poly(N,N-diethylacrylamide) (PDEAAm) as polymer backbone and poly(ethyleneglycol) as side chains were cross-linked on fluoropolymer substrates by low-pressure plasma treatment. All immobilized polymers exhibit a lo...
| Veröffentlicht in: | Langmuir : the ACS journal of surfaces and colloids. - 1985. - 20(2004), 23 vom: 09. Nov., Seite 10107-14 |
|---|---|
| 1. Verfasser: | |
| Weitere Verfasser: | , , |
| Format: | Aufsatz |
| Sprache: | English |
| Veröffentlicht: |
2004
|
| Zugriff auf das übergeordnete Werk: | Langmuir : the ACS journal of surfaces and colloids |
| Schlagworte: | Journal Article |
| Zusammenfassung: | Thin films of graft copolymers consisting of poly(N-isopropylacrylamide) (PNiPAAm) or poly(N,N-diethylacrylamide) (PDEAAm) as polymer backbone and poly(ethyleneglycol) as side chains were cross-linked on fluoropolymer substrates by low-pressure plasma treatment. All immobilized polymers exhibit a lower critical solution temperature between 34 and 40 degrees C. The swelling and collapsing of the hydrogels was examined with temperature-dependent spectroscopic ellipsometry. Two time ranges of swelling were observed: a fast 'dynamic' and a slow 'equilibrium' swelling. The dynamic swelling occurs within minutes or less, whereas the equilibrium swelling needs several days to complete. The surface-bound hydrogels show a shift in the transition temperature toward lower temperatures compared with the behavior in solution. Full reversibility of the dynamic swelling/collapsing was found, but the temperature scan exhibits a hysteresis between heating and cooling cycles. The PNiPAAm-containing hydrogels show a sharper transition compared to the PDEAAm-containing hydrogels, which is almost linear over a wide temperature range |
|---|---|
| Beschreibung: | Date Completed 10.04.2006 Date Revised 02.11.2004 published: Print Citation Status PubMed-not-MEDLINE |
| ISSN: | 1520-5827 |