Structural analysis of La/Al2O3 catalysts by La K-edge XAFS
Structural analysis of La/Al2O3 catalyst materials was carried out by means of XRD and La K-edge XAFS. Influences of loading amounts and treatment temperature on the local structure around La were investigated. La atoms are supported on gamma-Al2O3 in a highly dispersed form when a loading amount is...
| Veröffentlicht in: | Journal of synchrotron radiation. - 1994. - 8(2001), Pt 2 vom: 01. März, Seite 634-6 |
|---|---|
| 1. Verfasser: | |
| Weitere Verfasser: | , , , |
| Format: | Aufsatz |
| Sprache: | English |
| Veröffentlicht: |
2001
|
| Zugriff auf das übergeordnete Werk: | Journal of synchrotron radiation |
| Schlagworte: | Journal Article |
| Zusammenfassung: | Structural analysis of La/Al2O3 catalyst materials was carried out by means of XRD and La K-edge XAFS. Influences of loading amounts and treatment temperature on the local structure around La were investigated. La atoms are supported on gamma-Al2O3 in a highly dispersed form when a loading amount is less than 0.2 mmol g(Al2O3)(-1), and structural transformation of the La species does not take place in the temperature ranges of 873-1273 K. La species of highly loaded catalysts start to change their structure from oxide-like form to the aluminate at 1073 K. Formation of LaAlO3 perovskite on the catalyst surface requires a concentration of La atoms above 0.5 mmol g(Al2O3)(-1) (7.5 wt% as La2O3) |
|---|---|
| Beschreibung: | Date Completed 06.09.2001 Date Revised 05.06.2019 published: Print Citation Status PubMed-not-MEDLINE |
| ISSN: | 1600-5775 |