Lattice Engineering on Li2CO3-Based Sacrificial Cathode Prelithiation Agent for Improving the Energy Density of Li-Ion Battery Full-Cell

Détails bibliographiques
Publié dans:	Advanced materials (Deerfield Beach, Fla.). - 1998. - 36(2024), 13 vom: 10. März, Seite e2312159
Auteur principal:	Zhu, Yuanlong (Auteur)
Autres auteurs:	Chen, Yilong, Chen, Jianken, Yin, Jianhua, Sun, Zhefei, Zeng, Guifan, Wu, Xiaohong, Chen, Leiyu, Yu, Xiaoyu, Luo, Haiyan, Yan, Yawen, Zhang, Haitang, Zhang, Baodan, Kuai, Xiaoxiao, Tang, Yonglin, Xu, Juping, Yin, Wen, Qiu, Yongfu, Zhang, Qiaobao, Qiao, Yu, Sun, Shi-Gang
Format:	Article en ligne
Langue:	English
Publié:	2024
Accès à la collection:	Advanced materials (Deerfield Beach, Fla.)
Sujets:	Journal Article Li2CO3 decomposition anionic redox cathode prelithiation agent lattice engineering transition metal implantation

Description
Résumé:	© 2023 Wiley‐VCH GmbH. Developing sacrificial cathode prelithiation technology to compensate for active lithium loss is vital for improving the energy density of lithium-ion battery full-cells. Li2CO3 owns high theoretical specific capacity, superior air stability, but poor conductivity as an insulator, acting as a promising but challenging prelithiation agent candidate. Herein, extracting a trace amount of Co from LiCoO2 (LCO), a lattice engineering is developed through substituting Li sites with Co and inducing Li defects to obtain a composite structure consisting of (Li0.906Co0.043▫0.051)2CO2.934 and ball milled LiCoO2 (Co-Li2CO3LCO). Notably, both the bandgap and Li─O bond strength have essentially declined in this structure. Benefiting from the synergistic effect of Li defects and bulk phase catalytic regulation of Co, the potential of Li2CO3 deep decomposition significantly decreases from typical >4.7 to ≈4.25 V versus Li/Li+, presenting >600 mAh g-1 compensation capacity. Impressively, coupling 5 wt% Co-Li2CO3@LCO within NCM-811 cathode, 235 Wh kg-1 pouch-type full-cell is achieved, performing 88% capacity retention after 1000 cycles
Description:	Date Revised 28.03.2024 published: Print-Electronic Citation Status PubMed-not-MEDLINE
ISSN:	1521-4095
DOI:	10.1002/adma.202312159