Electrostrictive and photoluminescent properties in Pr-doped (Ba,Sr)(Ti,Al)O3 ceramics
Pr3(+)-doped (Ba,Sr)(Ti,Al)O3 ceramics were prepared using a conventional solid-state reaction technique. Multiple functions of electrostriction and photoluminescence were realized in the ceramics. Red emission (614 nm) was observed in the samples, and the intensity reached its largest value in the...
| Veröffentlicht in: | IEEE transactions on ultrasonics, ferroelectrics, and frequency control. - 1986. - 53(2006), 11 vom: 21. Nov., Seite 1969-73 |
|---|---|
| 1. Verfasser: | |
| Weitere Verfasser: | , |
| Format: | Aufsatz |
| Sprache: | English |
| Veröffentlicht: |
2006
|
| Zugriff auf das übergeordnete Werk: | IEEE transactions on ultrasonics, ferroelectrics, and frequency control |
| Schlagworte: | Journal Article |
| Zusammenfassung: | Pr3(+)-doped (Ba,Sr)(Ti,Al)O3 ceramics were prepared using a conventional solid-state reaction technique. Multiple functions of electrostriction and photoluminescence were realized in the ceramics. Red emission (614 nm) was observed in the samples, and the intensity reached its largest value in the sample of 40 mol% Sr addition. Although the electrostrictive strain decreased in the Pr and Al doped samples, the temperature dependence is remarkably improved comparable to the undoped sample |
|---|---|
| Beschreibung: | Date Completed 13.12.2006 Date Revised 17.09.2019 published: Print Citation Status PubMed-not-MEDLINE |
| ISSN: | 1525-8955 |